Binder compositions for fiber mats, and fiber mats and articles comprising them
Aqueous binder compositions for fiber mats include a urea-formaldehyde resin and an aqueous emulsion of a copolymer prepared by polymerization of a monomer mixture including styrene, an alkyl(meth)acrylate, acrylonitrile, and an unsubstituted or substituted acrylamide. Even when used in relatively low concentration, the copolymer provides improved physical properties to the fiber mat. The fiber mats can be used in composite flooring, asphalt roofing shingles, siding, and dry wall.
1. An aqueous binder composition for use in making fiber mats, the binder composition comprising:
a urea-formaldehyde resin; and
an aqueous emulsion of a copolymer prepared by polmerization of a mixture comprising about 20 wt % to about 60 wt % styrene, about 20 wt % to about 50 wt % of an alkyl (meth)acrylate, about 5 wt % to about 30 wt % acrylonitrile, and about 1 wt % to about 15 wt % of an unsubstituted or substituted acrylamide, where all weight percents are based on a total weight of the mixture.
2. The aqueous binder composition of claim 1 , wherein the alkyl (meth)acrylate is a C 1 -C 6 alkyl (meth)acrylate.
3. The aqueous binder composition of claim 1 , wherein the alkyl (meth)acrylate comprises butyl acrylate.
4. The aqueous binder composition of claim 1 , wherein the alkyl (meth)acrylate comprises ethyl acrylate.
5. The aqueous binder composition of claim 1 , wherein the unsubstituted or substituted acrylamide is selected from the group consisting of acrylamide, methacrylamide, N-methylolacrylamide, N-methylolmethacrylamide, and mixtures thereof.
6. The aqueous binder composition of claim 1 , wherein the unsubstituted or substituted acrylamide comprises acrylamide and N-methylolacrylamide.
7. The aqueous binder composition of claim 1 , wherein the mixture further comprises a silane monomer comprising at least one polymerizable carbon-carbon double bond and at least one hydrolyzable group.
8. The aqueous binder composition of claim 7 , wherein the silane monomer is selected from the group consisting of gamma-methacryloxypropyltriethoxysilane, beta-methacryloxyethyltrimethoxysilane, beta-methacryloxyethyltriethoxysilane, beta-methacryloxyethylmethyidimethoxysilane, beta-methacryloxyethylmethyidiethoxysilane, beta-methacryloxyethyldimethoxysilane, beta-methacryloxyethyldimethylethoxsilane, beta-methacryloxyethylyrichlorosilane, gamma-methacryloxypropyltrimethoxysilane, gamma-methacryloxpropylmethyldimethoxysilane, gamma-methacryloxypropylmethyldiethoxysilane, gamma-methacryloxypropyldimethoxysilane, gamma-methacryloxpropyldimethylethoxysilane, beta-acryloxethyltrimethoxysilane, beta-acryloxyethyltriethoxysilane, beta-acryloxyethylmethyidimethoxysilane, beta-acryloxyethylmethyidiethoxysilane, beta-acryloxyethyldimethylmethoxysilane, beta-acryloxyethyldimethylethoxysilane, beta-acryloxyethyltrichlorosilane, gamma-acryloxypropyltrimethoxysilane, gamma-acryloxypropylmethyldimethoxysiane, gamma-acryloxypropylmethyldiethoxysilane, gamma-acryloxpropyldimethylmethoxysilane, gamma-acryloxypropyldimethylethoxysilane, beta-styrylethyltrimethoxysilane, vinyltriacetoxysilane, vinylethoxydimethoxysilane, vinylmethyldimethoxysilane, vinylmethyldiethoxysilane, vinyltris(2-methoxyethoxy)silane, and mixtures thereof.
9. The aqueous binder composition of claim 7 , wherein the silane monomer comprises gamma-methacryloxypropyltriethoxysilane.
10. The aqueous binder composition of claim 1 , wherein the mixture further comprises poly(vinyl alcohol).
11. The aqueous binder composition of claim 1 , wherein the mixture further comprises starch.
12. The aqueous binder composition of claim 1 , wherein the mixture further comprises a crosslinking monomer comprising at least two polymerizable carbon-carbon double bonds.
13. The aqueous binder composition of claim 1 , wherein the mixture is free of maleic anhydride.
14. The aqueous binder composition of claim 1 , wherein the mixture is free of butadiene.
15. The aqueous binder composition of claim 1 , further comprising poly(styrene-maleic anhydride).
16. The aqueous binder composition of claim 1 , wherein the composition is free of poly(styrene-maleic anydride).
17. The aqueous binder composition of claim 1 , wherein the mixture further comprises itaconic acid, gamma-methacryloxpropltriethoxysilane, and a crosslinking monomer, wherein the alkyl (meth)acrylate comprises butyl acrylate and the unsubstituted or substituted acrylamide comprises acrylamide and N-methylolacryiamide, and wherein the mixture comprises about 30 wt % to about 60 wt % styrene, about 20 wt % to about 40 wt % butyl acrylate, about 10 wt % to about 25 wt % acrylonitrile, about 0.5 wt % to about 4 wt % acrylamide, about 1 wt % to about 6 wt % N-methylolacrylamide, about 0.1 wt % to about 3 wt % itaconic acid, about 0.1 wt % to about 3 wt % gamma-methacryloxpropyltriethoxysilane, and about 0.2 wt % to about 4 wt % of the crosslinking monomer, where all weight percents are based on the total weight of the mixture.
18. The aqueous binder composition of claim 1 , where the mixture further comprises itaconic acid, gamma-methacryloxpropylthriethoxysilane, a crosslinking monomer, and poly(vinyl alcohol), wherein the alkyl (meth)acrylate comprises butyl acrylate and the unsubstituted or substituted acrylamide comprises acrylamide and N-methylolacrylarnide, and wherein the mixture comprises about 30 wt % to about 60 wt % styrene, about 20 wt % to about 40 wt % butyl acrylate, about 10 wt % to about 25 wt % acrylonitrile, 0.5 wt % to about 4 wt % acrylamide, about 1 wt % to about 6 wt % N-methylolacrylamide, about 0.1 wt % to about 3 wt % itaconic acid, about 0.1 wt % to about 3 wt % gamma-methacryloxypropyltriethoxysilane, about 0.2 wt % to about 4 wt % of the crosslinking monomer, and about 5 wt % to about 20 wt % poly(vinyl alcohol), where all weight percents are based on the total weight of the mixture.
19. The aqueous binder composition of claim 1 , where the mixture further comprises itaconic acid, a crosslinking monomer, and starch, wherein the alky (meth)acrylate comprises ethyl acrylate and the unsubstituted or substituted acrylamide comprises acrylamide and N-methylolacrylamide, and wherein the mixture comprises about 40 wt % to about 60 wt % ethyl acrylate, about 20 wt % to about 40 wt % styrene, about 5 wt % to about 20 wt % acrylonitrile, about 0.2 wt % to about 3 wt % acrylamide, about 1 wt % to about 6 wt % N-methylolacrylamide, about 0.1 wt% to about 3 wt % itaconic acid, about 0.2 wt % to about 4 wt % of the crosslinking monomer, and about 5 wt % to about 20 wt % starch, where all weight percents are based on the total weight of the mixture.
20. A non-woven fiber mat, comprising:
reinforcing fibers; and
a cured product of a curable binder composition comprising:
a urea-formaldehyde resin; and
an aqueous emulsion of a copolymer prepared by polymerization of a mixture comprising about 20 wt % to about 60 wt % styrene, about 20 wt % to about 50 wt % of an alkyl (meth)acrylate, about 5 wt % to about 30 wt % acrylonitrile, and about 1 wt % to about 15 wt % of an unsubstituted or substituted acrylamide, where all weight percents are based on a total weight of the mixture.
21. The non-woven fiber mat of claim 20 , wherein the reinforcing fibers are glass fibers.
22. A fiber mat faced gypsum wall board, comprising:
a gypsum core having a planar first face and a planar second face; and
a coated non-woven glass fiber mat facing material adhered to and covering at least one of the planar first face and the planar second face;
wherein the non-woven glass fiber mat facing material comprises a coating comprising a cured product of a curable binder composition comprising:
a urea-formaldehyde resin; and
an aqueous emulsion of a copolymer prepared by polymerization of a mixture comprising about 20 wt % to about 60 wt % styrene, about 20 wt % to about 50 wt % of an alkyl (meth)acrylate, about 5 wt % to about 30 wt % acrylonitrile, and about 1 wt % to about 15 wt % of an unsubstituted or substituted acrylamide, where all weight percents are based on a total weight of the mixture.