Primer for fluorocarbon polymer substrates
An aqueous primer dispersion which contains surfactant-stabilized polymer particles, an organic solvent and a mineral thicker, when coated onto a fluorocarbon substrate, significantly increase the bond strength between the fluorocarbon substrate and a subsequently applied water-derived protective coating, provided that the amount of surfactant-stabilized polymer particles in the aqueous primer dispersion, if any, is about 8 wt. % or less.
1. An aqueous primer dispersion for use in coating a fluorocarbon substrate to increase the adhesive strength between the fluorocarbon substrate and a subsequently applied water-derived protective coating, the aqueous primer dispersion consisting essentially of
(1) about 0.5-10 wt. % of at least one aqueous acrylic polymer source dispersion containing acrylic polymer particles,
(2) about 25-400 wt. % based on the weight of all polymer particles in the aqueous primer dispersion of an organic solvent capable of softening the acrylic polymer particles, and
(3) a mineral thickener, wherein the weight ratio of mineral thickener to all of the polymer particles in the aqueous primer dispersion is between about 1:1 to 7.5:1,
wherein the total amount of aqueous dispersions used to make the aqueous primer dispersion is about 10 wt. % or less, and further wherein the total amount of all polymer particles in the aqueous primer dispersion which are surfactant-stabilized, if any, is no more than 8 wt. %, and further wherein essentially all of the polymer particles in the aqueous primer dispersion are formed from an acrylic polymer.
2. The aqueous primer dispersion of claim 1 , wherein the weight ratio of mineral thickener to polymer particles is between about 1.5:5 to 5:1.
3. The aqueous primer dispersion of claim 2 , wherein the weight ratio of mineral thickener to polymer particles is between about 2:1 to 4:1.
4. The aqueous primer dispersion of claim 1 , wherein the total amount of aqueous dispersions used to make the aqueous primer dispersion is about 6 wt. % or less.
5. The aqueous primer dispersion of claim 4 , wherein the organic solvent is at least one of pyrrolidones having a hydrogen or C 1 -C 4 alkyl attached to the nitrogen of the pyrrolidone ring, lactones, organic esters have 6-10 carbon atoms, propylene carbonate, C 1 -C 8 propionates, glycol ethers, isobutyl isobutyrate, mixtures of esters containing at least three of hexyl, heptyl, octyl, nonyl and decyl acetates and dimethyl sulfoxide.
6. The aqueous primer dispersion of claim 5 , wherein the organic solvent includes N-methylpyrrolidone.
7. The aqueous primer dispersion of claim 6 , wherein the organic solvent includes dimethyl sulfoxide.
8. The aqueous primer dispersion of claim 1 , wherein the organic solvent is at least one of pyrrolidones having a hydrogen or C 1 -C 4 alkyl attached to the nitrogen of the pyrrolidone ring, lactones, organic esters have 6-10 carbon atoms, propylene carbonate, C 1 -C 8 propionates, glycol ethers, isobutyl isobutyrate, mixtures of esters containing at least three of hexyl, heptyl, octyl, nonyl and decyl acetates and dimethyl sulfoxide.
9. The aqueous primer dispersion of claim 8 , wherein the organic solvent includes N-methylpyrrolidone.
10. The aqueous primer dispersion of claim 9 , wherein the organic solvent includes dimethyl sulfoxide.
11. The aqueous primer dispersion of claim 10 , wherein the mineral filler is a synthetic colloidal smectite clay.
12. The aqueous primer dispersion of claim 10 , wherein the mineral filler is a synthetic colloidal, thixotropic clay.
13. The aqueous primer dispersion of claim 9 , wherein the mineral filler is a synthetic colloidal, thixotropic clay.
14. A process for increasing the bond strength between a fluorocarbon substrate and a water-based protective coating on the substrate comprising depositing an aqueous primer dispersion on the substrate to form a coherent primer layer before application of the protective coating, wherein the aqueous primer dispersion comprises the dispersion of claim 1 .