Stable ethylpolysilicates with greater than fifty percent available SiO
A stable MQ resin solution with over 50% SiO 2 and having viscosity of 50 cps at 25° C. to about 750 cps at 25° C. and which is essential free of monomer is disclosed. The stable resin solution is made by a two step addition of catalysts wherein a hydrolysis catalysts, as for example, hydrochloric acid is added initially and a second catalysts such as Phosphonitrilic chloride trimer is added subsequently.
1. A stable ethylsilicate polymer in liquid form, said polymer comprising between about 50% by-weight and 60% by-weight silica, having a viscosity of about 10 cps at 25° C. and up to a viscosity of 1000 cps at 25° C. and remaining in liquid form after heating at 55° C. for 20 days and wherein said polymer is free of monomer.
2. A stable ethylsilicate polymer according to claim 1 in which the specific gravity is between about 1.19 and 1.22.
3. A stable ethylsilicate polymer according to claim 2 in which the molecular distribution includes molecular weights higher than 4956.
4. A stable ethylsilicate polymer according to claim 2 in which the molecular weight distribution is about Mp 34,600, Mn is about 18,000, Mw is about 51,100, Mz is about 10,700 and PD is about 2.8 and wherein Mp is the molecular weight at peak, Mn is the number average molar mass, Mw is the weight average molar mass, Mz is the average molar mass and PD is polydisparity.
5. A stable ethylsilicate polymer according to claim 2 which contains about 54% silica.
6. A stable ethylsilicate polymer as set forth in claim 1 formed by a processes that including using a phosphonitrilic chloride (PNC) catalyst.
7. A stable ethylsilicate polymer as set forth in claim 6 wherein the process includes adding a hydrolysis catalyst to a tetraethyl orthosilicate (TEOS) monomer prior to using the PNC catalyst.