Production of carbon nanotubes
View Patent ↗A method and apparatus for manufacture of carbon nanotubes, in which a substrate is contacted with a hydrocarbonaceous feedstock containing a catalytically effective metal to deposit the feedstock on the substrate, followed by oxidation of the deposited feedstock to remove hydrocarbonaceous and carbonaceous components from the substrate, while retaining the catalytically effective metal thereon, and contacting of the substrate having retained catalytically effective metal thereon with a carbon source material to grow carbon nanotubes on the substrate. The manufacture can be carried out with a petroleum feedstock such as an oil refining atmospheric tower residue, to produce carbon nanotubes in high volume at low cost. Also disclosed is a composite including porous material having single-walled carbon nanotubes in pores thereof.
1. A method of forming carbon nanotubes, comprising:
depositing one or more carbon compounds on a substrate, wherein the one or more carbon compounds comprise a catalytically effective metal;
combusting the one or more carbon compounds under oxidizing conditions to produce a catalytically effective metal-containing substrate; and
contacting a carbon source material with the catalytically effective metal-containing substrate under sufficient growth conditions to grow carbon nanotubes on the substrate;
wherein the carbon compound comprises a petroleum feedstock, a residual oil feedstock, or an oil refining atmospheric tower residue.
2. The method of claim 1 , wherein the catalytically effective metal comprises nickel or iron, and the carbon source material comprises a hydrocarbon material.
3. The method of claim 1 , wherein the carbon source material comprises a petroleum feedstock, a residual oil feedstock, or an oil refining atmospheric tower residue.
4. The method of claim 1 , wherein said petroleum feedstock, said residual oil feedstock, or said oil refining atmospheric tower residue comprises nickel porphyrins.
5. The method of claim 2 wherein said hydrocarbon material comprises at least one unsaturated hydrocarbon.
6. The method of claim 5 wherein said at least one unsaturated hydrocarbon is volatilizable into hydrocarbon vapor so as to facilitate contact with said catalytically effective metal.
7. The method of claim 5 wherein said at least one unsaturated hydrocarbon is selected from the group consisting of alkenes, alkynes, cycloalkenes, cycloalkynes, aryls, arylalkyls, and alkaryls.
8. The method of claim 3 wherein said petroleum feedstock, said residual oil feedstock, or said oil refining atmospheric tower residue contains nickel porphyrins.
9. The method of claim 4 , wherein said nickel porphyrins exhibit nickel concentrations within the range of approximately one part per million by weight (ppm wt.) to approximately 100 parts per million by weight (ppm wt.).
10. The method of claim 4 , wherein said nickel porphyrins exhibit nickel concentrations greater than 100 parts per million by weight (ppm wt.).
11. The method of claim 1 , wherein said petroleum feedstock, said residual oil feedstock, or said oil refining atmospheric tower residue contains iron at concentrations within the range of approximately one part per million by weight (ppm wt.) to approximately 50 parts per million by weight (ppm wt.).
12. The method of claim 1 wherein said substrate is composed of a material selected from the group consisting of silica, alumina, aluminosilicates, kielselguhr, clays, and macroreticulate polymer.
13. The method of claim 1 wherein said substrate is formed of finely divided microparticles.
14. The method of claim 13 wherein said finely divided microparticles are microspheres, microflakes, or microrods.
15. The method of claim 1 wherein said substrate comprises an inert silica-alumina matrix of calcined kaolin mircospheres.
16. The method of claim 1 wherein the one or more carbon compounds are deposited on the substrate at a temperature within the range of 480° C. to 750° C.
17. The method of claim 1 wherein the one or more carbon compounds are deposited on the substrate at a temperature within the range of 510° C. to 710° C.
18. The method of claim 1 wherein the one or more carbon compounds are deposited on the substrate at a temperature within the range of 520° C. to 650° C.
19. The method of claim 1 wherein the one or more carbon compounds are deposited on the substrate at a temperature within the range of 526° C. to 620° C.
20. The method of claim 1 wherein the one or more carbon compounds are deposited on the substrate at a pressure within the range of 15 psig to 50 psig.
21. The method of claim 1 wherein the one or more carbon compounds are deposited on the substrate at a flow rate within the range of 5 kg/hour to 20 kg/hour.
22. The method of claim 1 , wherein the same material is used as the one or more carbon compounds comprising a catalytically effective metal and the carbon source material.
23. The method of claim 1 , wherein combusting the one or more carbon compounds under oxidizing conditions comprises contacting the substrate with an oxidant gas.
24. The method of claim 23 , wherein the one or more carbon compounds are oxidized at a temperature within a range of 550° C. and 870° C.
25. The method of claim 23 , wherein the oxidant gas comprises one or more members selected from the group consisting of carbon monoxide, carbon dioxide, oxygen, air, and oxygen-enriched air.
26. The method of 1 , wherein sufficient growth conditions comprise temperature within a range of 300° C. and 700° C., pressure within a range of 1 and 200 pounds-force per square inch gauge (psig), and contacting time within a range of 0.1 second to 10 minutes.