Aqueous method for making magnetic iron oxide nanoparticles
View Patent ↗The invention discloses an aqueous method of making polymer coated superparamagnetic nanoparticles. The method comprises providing a mixture of iron salts in an aqueous solution of hydrochloric acid. A solution of ammonium hydroxide is added to the mixture and stirred. Stirring continues with an aqueous solution of one or more biocompatible polymers so as to promote formation of polymer coated iron nanoparticles in suspension, wherein optionally at least one of the polymers in the coating may be aminated. Centrifuging the suspension leaves a supernatant without large particles. Filtering the supernatant through an ultrafiltration membrane and collecting the filtrate recovers polymer coated nanoparticles. Crosslinking the polymer is effected by treatment with a solution of epichlorohydrin and sodium hydroxide while stirring vigorously for up to about eight hours. Optionally aminating the polymer may be accomplished by treatment with ammonia after crosslinking and then removing remaining free epichlorohydrin. Nanoparticles made by the method are included in the invention.
1. An aqueous method of making polymer coated superparamagnetic nanoparticles, the method comprising:
(a) providing a mixture of iron salts in aqueous hydrochloric acid;
(b) combining a solution of ammonium hydroxide with the mixture of (a) and stirring for a time sufficient for formation of a suspension of iron oxide nanoparticles;
(c) adding to the suspension of (b) one or more aqueous biocompatible polymers, thereby coating the nanoparticles with polymer in the presence of unreacted reagents specified in (a) and (b);
(d) centrifuging the suspension, rendering a supernatant without large particles;
(e) filtering the supernatant through an ultrafiltration membrane and collecting the filtrate containing the polymer coated nanoparticles;
(f) crosslinking the polymer coating by treating the nanoparticles with epichlorohydrin and sodium hydroxide while mixing;
(g) aminating any un-aminated crosslinked polymer remaining by treating with ammonia; and
(h) removing free epichlororohydrin from the suspension.
2. The method of claim 1 , wherein the iron salts are selected from FeCl 2 , FeCl 3 , and combinations thereof.
3. The method of claim 1 , wherein the biocompatible polymer comprises dextran.
4. Nanoparticles comprising iron-oxide coated with a crosslinked aminated biocompatible polymer containing dextran, said nanoparticles having a size range of approximately 100-500 nm, and made according to the method of claim 1 .