METHOD AND SORBANT FOR REMOVING CONTAMINATES FROM WATER
A method and corresponding sorbant for removing dissolved contaminants, such as arsenate, from water. The sorbant comprises an oxide of titanium and a sulfate salt, such as calcium sulfate.
1 . A method for removing dissolved contaminants from water comprising the step of contacting a sorbant with the water, the sorbant comprising at least about 50 wt. % of an oxide of titanium and at least about 3 wt. % of a sulfate salt having a solubility in water of less than 0.5 grams per liter of water; and on an elemental analysis basis at least about 20 wt. % titanium and at least about 1 wt. % sulfur.
2 . The method of claim 2 wherein the sorbant comprises at least about 80 wt. % of an oxide of titanium and at least about 5 wt. % of a sulfate salt.
3 . The method of claim 2 wherein the sorbant comprises about 85 to about 95 wt. % of an oxide of titanium and about 5 to about 15 wt. % of a sulfate salt.
4 . The method of claim 2 wherein the sorbant comprises about 87 to about 93 wt. % of an oxide of titanium and about 7 to about 13 wt. % of a sulfate salt.
5 . The method of claim 4 wherein the sulfate salt comprises calcium sulfate.
6 . The method of claim 2 wherein the sorbant comprises less than about 6 wt. % calcium on an elemental analysis basis.
7 . The method of claim 5 wherein the sorbant comprises less than about 5 wt. % calcium on an elemental analysis basis.
8 . The method of claim 2 wherein the sorbant comprises from about 1 to about 5 wt.
9 . The method of claim 2 wherein the sorbant comprises from about 1.5 to about 4 wt. % sulfur and about 45 to about 55 wt. % titanium on an elemental analysis basis.
10 . A sorbant comprising about 85 to about 95 wt. % of an oxide of titanium and about 5 to about 15 wt. % of a sulfate salt having a solubility in water of less than 0.5 grams per liter of water, wherein the sorbant comprises from about 1 to about 5 wt. % sulfur and about 35 to about 55 wt. % titanium on an elemental analysis basis, and wherein the oxide of titanium is primarily titanium dioxide.
11 . The sorbant of claim 10 wherein the sulfate salt comprises calcium sulfate and wherein the sorbant comprises less than about 6 wt. % calcium on an elemental analysis basis.
12 . The sorbant of claim 11 wherein the sorbant comprises about 87 to about 93 wt. % of an oxide of titanium and about 7 to about 13 wt. % of calcium sulfate.