Cross-linked thermoplastic polyurethane/polyurea and method of making same
View Patent ↗A cross-linked thermoplastic polyurea is formed by heating a mixture containing a thermoplastic urethane base material, a monomeric and/or polymeric di-isocyanate comprising between 1 to 10% of the total weight of the mixture, and a diamine comprising between 1 to 10% of the total weight of the mixture. A thermoplastic polyurethane may be formed by substituting hydroquinone for the diamine. The mixture is heated to a temperature within the range of 250° F. to 550° F. The heated mixture, which is flowable, is then injected into at least one injection molding device. The mixture is then cured at a temperature between 150° F. to 250° F. for a period of time between 2 and 36 hours. The cross-linked thermoplastic polyurethane/polyurea retains the excellent flowability characteristics of a thermoplastic urethane while the same time exhibits good abrasion, tensile strength, rebound, and compression set characteristics which are similar to those found in thermoset urethanes.
1. A method of making a cross-linked thermoplastic polyurea comprising the steps of:
heating a dry mixture to a temperature within the range of 250° F. to 550 ° F. within a mixing barrel to created a heated partially cross-linked mixture, the dry mixture comprising a thermoplastic urethane base material, a di-isocyanate comprising between 1 to 10% of the total weight of the mixture, the di-isocyanate being one of monomeric or polymeric, and a diamine comprising between 1 to 10% of the total weight of the mixture, the diamine selected from the group consisting of 4, 4′ methylene-bis-(3-chloro-2, 6-diethylaniline) and 4, 4′ methylene-bis-(2, 6-diethylaniline);
injecting the heated partially cross-linked mixture into at least one injection mold cavity; and
curing the injected material at a temperature between 150° F. to 250° F. for a period of time between 2 and 36 hours.
2. The method of claim 1 wherein the di-isocynate comprises 4, 4′ diphenylmethane di-isocyanate.