Cobalt-molybdenum sulfide catalyst materials and methods for ethanol production from syngas
The present invention provides methods and compositions for the chemical conversion of syngas to alcohols. The invention includes catalyst compositions, methods of making the catalyst compositions, and methods of using the catalyst compositions. Certain embodiments teach compositions for catalyzing the conversion of syngas into products comprising at least one C 1 -C 4 alcohol, such as ethanol. These compositions generally include cobalt, molybdenum, and sulfur. Preferred catalyst compositions for converting syngas into alcohols include cobalt associated with sulfide in certain preferred stoichiometries as described and taught herein.
1. A composition for catalyzing the conversion of syngas into products comprising at least one C 1 -C 4 alcohol, said composition comprising cobalt, molybdenum, and sulfur,
wherein at least some of said cobalt and some of said sulfur are present as a cobalt-sulfur association, and
wherein the molar ratio of sulfur to cobalt (S:Co) in said association is at least 1.2,
said molar ratio S:Co calculated after assigning some of said sulfur to molybdenum by assuming all molybdenum is present in said composition as MoS 2 .
2. The composition of claim 1 , wherein said molar ratio S:Co is at least 1.5.
3. The composition of claim 2 , wherein said molar ratio S:Co is at least 2.0.
4. The composition of claim 1 , wherein said molar ratio S:Co is between about 2.0 and about 4.0.
5. The composition of claim 1 , wherein said cobalt is present in an amount between about 3 wt % and about 21 wt % of said composition.
6. The composition of claim 5 , wherein said cobalt is present in an amount between about 10 wt % and about 16 wt % of said composition.
7. The composition of claim 1 , wherein said molybdenum is present in an amount between about 33 wt % and about 56 wt % of said composition.
8. The composition of claim 1 , wherein the molar ratio of said molybdenum to said cobalt is from about 1.5 to about 8.
9. The composition of claim 8 , wherein said molar ratio of said molybdenum to said cobalt is from about 2.
10. The composition of claim 1 , wherein said sulfur is present in a total amount of at least 40 wt % of said composition.
11. The composition of claim 10 , wherein said sulfur is present in a total amount between about 42 wt % and about 44 wt % of said composition.
12. The composition of claim 1 , wherein said molar ratio S:Co is calculated after assigning some of said sulfur to molybdenum by assuming all molybdenum is present in said composition as MoS 2 , and after subtracting any elemental sulfur present.
13. The composition of claim 1 or 12 , wherein said molar ratio S:Co is further calculated after subtracting any sulfur that is soluble in 3 N HCl.
14. The composition of claim 1 , wherein said sulfur includes elemental sulfur in an amount of at least 100 ppm of said composition.
15. The composition of claim 14 , wherein said sulfur includes elemental sulfur in an amount of at least between about 150 ppm and about 5000 ppm.
16. The composition of claim 15 , wherein said sulfur includes elemental sulfur in an amount between about 300 ppm and about 1000 ppm.
17. The composition of claim 1 , wherein at least 0.02% of said sulfur is capable of leaching into chloroform at 55° C.
18. The composition of claim 17 , wherein at least 0.05% of said sulfur is capable of leaching into chloroform at 55° C.
19. The composition of claim 17 , wherein between about 0.02% and about 0.1% of said sulfur is capable of leaching into chloroform at 55° C.
20. The composition of claim 1 , wherein less than about 8% of said cobalt is capable of leaching into a 3N HCl solution at 90° C.
21. The composition of claim 20 , wherein less than about 3% of said cobalt is capable of leaching into a 3N HCl solution at 90° C.
22. The composition of claim 21 , wherein substantially no cobalt is capable of leaching into a 3N HCl solution at 90° C.
23. The composition of claim 1 , wherein less than about 0.5% of said molybdenum is capable of leaching into a 3N HCl solution at 90° C.
24. The composition of claim 23 , wherein less than about 0.3% of said molybdenum is capable of leaching into a 3N HCl solution at 90° C.
25. The composition of claim 24 , wherein substantially no molybdenum is capable of leaching into a 3N HCl solution at 90° C.
26. The composition of claim 1 , further comprising one or more base promoters selected from the group consisting of potassium, rubidium, cesium, barium, strontium, scandium, yttrium, lanthanum, cerium, and any combinations thereof.
27. A catalyst composition for catalyzing the conversion of syngas into at least some ethanol, said composition comprising 13-15 wt % total cobalt, 40-45 wt % total molybdenum, at least 40 wt % total sulfur, and at least 0.01 wt % of a base promoter, wherein:
(i) said total sulfur includes between 250-750 ppm elemental sulfur;
(ii) at least some of said total cobalt and some of said total sulfur are present as a cobalt-sulfur association having a molar ratio of sulfur to cobalt (S:Co) of at least 2.0, said molar ratio S:Co calculated assuming all molybdenum is present as MoS 2 , and after subtracting sulfur that is capable of leaching into chloroform or 3 N HCl at 25° C.;
(iii) less than about 3% of said total cobalt is capable of leaching into a 3 N HCl solution at 90° C.; and
(iv) less than about 0.5% of said total molybdenum is capable of leaching into a 3N HCl solution at 90° C.