Manganese oxide nanowires, films, and membranes and methods of making
Nanowires, films, and membranes comprising ordered porous manganese oxide-based octahedral molecular sieves and methods of making the same are disclosed. A method for forming nanowires includes hydrothermally treating a chemical precursor composition in a hydrothermal treating solvent to form the nanowires, wherein the chemical precursor composition comprises a source of manganese cations and a source of counter cations, and wherein the nanowires comprise ordered porous manganese oxide-based octahedral molecular sieves.
1. A method for forming nanowires, the method comprising:
hydrothermally treating a chemical precursor composition in a hydrothermal treating solvent to form the nanowires, wherein the chemical precursor composition comprises a source of manganese cations and a source of counter cations, and wherein the nanowires comprise ordered porous manganese oxide-based octahedral molecular sieves;
forming a suspension of the nanowires;
contacting the suspension of the nanowires with a substrate at a temperature and for a time effective to self-assemble a film comprising the nanowires; and
removing the substrate from the film to form a free standing membrane comprising the nanowires.
2. The method of claim 1 , wherein the source of manganese cations comprises a manganese salt with an anion comprising a sulfate, persulfate, sulfide, nitrite, nitrate, phosphate, halide, perchlorate, carbonate, acetate, alkoxide, permanganate, dichromate, formate, chromate, oxalate, acetate, or a combination comprising at least one of the foregoing anions, or hydrates of one of the foregoing salts.
3. The method of claim 1 , wherein the source of counter cations comprises a counter cation salt with an anion comprising a sulfate, persulfate, sulfide, nitrite, nitrate, phosphate, halide, perchlorate, carbonate, acetate, alkoxide, permanganate, dichromate, formate, chromate, oxalate, acetate, or a combination comprising at least one of the foregoing anions, or a hydrate of one of the foregoing salts.
4. The method of claim 1 , wherein a counter cation is a cation of H, Li, K, Rb, Cs, Ba, Mg, Ca, Pb, Co, Ni, Cu, Fe, V, Nb, Ta, Cr, Mo, Ag, W, Zr, Ti, Cd, Zn, Ln, ammonium, or a combination comprising at least one of the foregoing cations.
5. The method of claim 1 , wherein the chemical precursor composition further comprises a source of framework substituting cations, wherein a framework substituting cation comprises a cation of H, Li, K, Rb, Cs, Ba, Mg, Ca, Pb, Co, Ni, Cu, Fe, V, Nb, Ta, Cr, Mo, Ag, W, Zr, Ti, Cd, Zn, Ln, or a combination comprising at least one of the foregoing cations.
6. The method of claim 1 , wherein hydrothermally treating comprises heating in a sealed reaction vessel at about 150° C. to about 350° C. for greater than about 12 hours.
7. The method of claim 1 , further comprising isolating the nanowires by filtration.
8. The method of claim 1 , further comprising subjecting the nanowires to an ion exchange step, wherein a portion or all of the counter cations are replaced with different counter cations.
9. The method of claim 1 , wherein the nanowires have average diameters of about 5 nanometers to about 100 nanometers and have average lengths of greater than about 10 micrometers.
10. The method of claim 1 , wherein the contacting occurs at about 50° C. to about 150° C. for greater than about 3 hours.
11. The method of claim 1 , wherein an average thickness of the film or membrane is about 1 micrometer to about 10 millimeters.
12. The method of claim 1 , further comprising annealing the membrane at about 80° C. to about 200° C. for greater than about 1 hour.