Finely Divided Glass Filler For Rubber Latex Adhesive Compositions
Embodiments relate to adhesive compositions for use in carpet backing and other textiles. The adhesive compositions contain a rubber latex formulation including a conjugated diene, finely divided glass particles, and optionally additional fillers. The adhesive compositions provide carpet products having improved lamination strength, and enable higher run speeds, and consequently, increased carpet manufacturing capacity.
1 . A carpet backing comprising an adhesive composition adhered to a carpet substrate, said adhesive composition comprising a rubber latex comprised of at least one conjugated diene, finely divided glass particles, and at least one filler.
2 . The carpet backing as claimed in claim 1 , wherein the at least one filler is selected from the group consisting of calcium carbonate, aluminum hydroxide, magnesium hydroxide, clay, barium sulfate, silicic acid, silicate, titanium oxide, magnesium carbonate, and mixtures thereof.
3 . The carpet backing as claimed in claim 2 , wherein the at least one filler is calcium carbonate.
4 . The carpet backing as claimed in claim 1 , wherein the at least one filler is present in an amount of from about 1 part by weight to about 5 parts by weight, per weight of rubber latex.
5 . The carpet backing as claimed in claim 1 , wherein the finely divided glass is selected from the group consisting of powdered glass, powdered sand, powdered quartz, powdered silica-containing ceramics, and mixtures thereof.
6 . The carpet backing as claimed in claim 1 , wherein the finely divided glass comprises particles having an average mesh size of from about 40 to about 250 mesh.
7 . The carpet backing as claimed in claim 1 , wherein the finely divided glass particles are present in an amount of from about 0.1 to about 1.5 parts by weight, based on the weight of the rubber latex.
8 . The carpet backing as claimed in claim 7 , wherein the finely divided glass particles are present in an amount of from about 0.15 to about 0.50 parts by weight, based on the weight of the rubber latex.
9 . The carpet backing as claimed in claim 1 , wherein the conjugated diene is selected from the group consisting of butadiene, isoprene, chloroprene.
10 . The carpet backing as claimed in claim 1 , wherein the rubber latex is comprised of at least one copolymer of a conjugated diene and an ethylenecially unsaturated monomer.
11 . The carpet backing as claimed in claim 1 , wherein the composition cures faster than an adhesive composition that does not contain finely divided glass particles.
12 . The carpet backing as claimed in claim 11 , wherein the curing time is from about 10 to about 50% faster.