A process for obtaining tantalum powder from tantalum containing scrap material is provided. The process includes selecting source material, such as from sintered anodes for capacitors, hydriding the source material, milling to desired particle size and surface area, dehydriding, deoxidizing, agglomerating, sifting, and acid treating to obtain tantalum powder of a desired size and purity.
1. A method of producing powder from reclaimed capacitor anodes of a material comprising sintered tantalum powder around a central tantalum wire comprising the step of:
hydriding the material by heating the material in vacuum then backfilling with hydrogen;
lightly milling the hydrided anodes to liberate the tantalum wire;
sifting the milled anodes to separate the tantalum wire from the powder;
heat treating the powder in one or more steps to dehydride, deoxidize, and agglomerate the powder; and
crushing the agglomerates and sifting to produce a particle size distribution capable of being pressed and sintered to re-form capacitor anodes.
2. The method of claim 1 further comprising the initial steps of sampling the anodes to determine initial contamination levels and treating the anodes to at least partially remove the contamination.
3. The method of claim 2 wherein the treating the anodes is done by acid leaching the anodes.
4. The method of claim 3 further comprising the steps of rinsing the acid treated anodes to remove acid residue and drying the rinsed anodes.
5. The method of claim 1 further wherein the capacitor anode contains an oxide film and further comprising the step of removing the oxide film by heating with Mg at sufficient temperature and time to at least partially remove the oxide film before the step of hydriding.