Advanced solid acid electrolyte composites
Solid acid/surface-hydrogen-containing secondary component electrolyte composites, methods of synthesizing such materials, electrochemical device incorporating such materials, and uses of such materials in fuel cells, membrane reactors and hydrogen separations are provided. The stable electrolyte composite material comprises a solid acid component capable of undergoing rotational disorder of oxyanion groups and capable of extended operation at a wide temperature range and a secondary compound with surface hydrogen atoms, which when intimately mixed, results in a composite material with improved conductivity, mechanical and thermal properties, when compared to pure solid acid compound.
1. A proton conducting membrane, said membrane comprising:
a solid acid component of the formula CsH 2 PO 4 , wherein said solid acid component is capable of conducting protons in a solid state through a superprotonic mechanism;
a secondary component having a plurality of surface hydrogen, comprising
at least one member selected from the group consisting of LaPO 4 *H 2 O(H 3 PO 4 ) g , SiC, C 6 H 3 (COOH) 3 , polybenzimidazole (PBI), polyimide and multi-walled fullerene, wherein
g is a non-negative real number from 1 to 4; and
a plurality of interfaces formed by said solid acid component and said secondary component, wherein said solid acid component and said secondary component interact to form a composite.
2. The proton conducting membrane of claim 1 , wherein said plurality of interfaces is formed by hydrogen bonding interactions between said solid acid component and said secondary component.
3. The proton conducting membrane of claim 1 , wherein said solid acid component comprises a plurality of solid acid particles.
4. The proton conducting membrane of claim 1 , wherein said secondary component comprises a plurality of secondary component particles.
5. The proton conducting membrane of claim 1 , further comprising a structural binder selected from the group consisting of a polymer, ceramic, glass, a metal, a nanostructure and a mixture thereof.
6. The proton conducting membrane of claim 1 , wherein said secondary component comprises a compound having the formula LaPO 4 *nH 2 O(H 3 PO 4 ) g .
7. The proton conducting membrane of claim 1 , wherein
said secondary component comprises polybenzimidazole.
8. The proton conducting membrane of claim 1 , having a conductivity from about 10 −3 Ω −1 cm −1 to about 0.2 Ω −1 cm −1 in the temperature range from about 130° C. to about 330° C.
9. The proton conducting membrane of claim 1 , further comprising a separate electrically conducting material.
10. The proton conducting membrane of claim 9 , wherein the conducting material is selected from the group consisting of a conducting polymer, a metal and a carbon material.
11. The proton conducting membrane of claim 1 , wherein said membrane has a proton conductivity of about 10 −5 Ω −1 cm −1 or higher at the temperature of utilization.
12. A fuel cell system comprising a proton conducting membrane in accordance with claim 1 , wherein the fuel cell system provides electrical power to an external device.
13. A proton conducting membrane, said membrane comprising:
a plurality of solid acid particles of the formula CsH 2 PO 4 , wherein said plurality of solid acid particles is capable of conducting protons in a solid state through a superprotonic mechanism;
a plurality of secondary component particles having a plurality of surface hydrogen, each particle comprising:
at least one member selected from the group consisting of LaPO 4 *H 2 O(H 3 PO 4 ) g , SiC, C 6 H 3 (COOH) 3 ,polybenzimidazole (PBI), polyimide and multi-walled fullerene, wherein
g is a non-negative real number from 1 to 4; and
a plurality of interfaces formed by said solid acid component particles and said secondary component particles, wherein said solid acid component and said secondary component interact to form a composite.
14. The proton conducting membrane of claim 13 , wherein each particle of said plurality of secondary particles has a dimension from about 5 nm to about 50 μm.
15. A method for preparing a proton conducting membrane, said method comprising:
contacting a solid acid component with a secondary component having a plurality of surface hydrogen under conditions sufficient to generate a composite, wherein said solid acid component interacts with said secondary component to form a plurality of interfaces,
wherein
said solid acid component is CsH 2 PO 4 ; and
said secondary component comprises at least one of
LaPO 4 *H 2 O(H 3 PO 4 ) g , SiC, C 6 H 3 (COOH) 3 , polybenzimidazole (PBI), polyimide and multi-walled fullerene, wherein
g is a non-negative real number from 1 to 4.
16. The method of claim 15 , further comprising contacting a structural binder.
17. The method of claim 15 , wherein said plurality of interfaces is formed by hydrogen bonding interactions between said solid acid component and said secondary component.