Methods of regeneration of SCR catalyst poisoned by phosphorous components in flue gas
A method of regeneration of a SCR catalyst for use in high temperature thermal processes such as in a power plant facility burning fossil fuels, bio-based fuels, or a combination thereof, wherein the catalyst is poisoned by phosphorous components in the flue gas and the catalyst is treated using a base, preferably an alkali metal hydroxide.
1. A method of regenerating a phosphorous-poisoned SCR catalyst, the method comprising treating the phosphorous-poisoned catalyst with an alkali metal hydroxide at a pH above 8.5.
2. The method according to claim 1 , wherein the alkali metal hydroxide is sodium hydroxide, potassium hydroxide, or a combination thereof.
3. A method of regenerating a phosphorous-poisoned SCR catalyst, the method comprising treating the phosphorous-poisoned catalyst with an alkali metal hydroxide at a pH in a range of from above about 10 to about 14 and a temperature up to about 176° F.
4. The method according to claim 3 , wherein the alkali metal hydroxide is sodium hydroxide, potassium hydroxide, or a combination thereof.
5. The method according to claim 3 , wherein the phosphorous-poisoned catalyst is treated in a soaking bath, an ultrasonic treatment solution, or a combination thereof.
6. The method according to claim 5 , wherein the bath or solution further comprises a surface active substance.
7. The method according to claim 3 , wherein the catalyst is treated at a temperature in a range of from about 60° F. to about 140° F.
8. The method according to claim 7 , wherein the catalyst is treated at a temperature in a range of from about 120° F. to about 130° F.
9. The method according to claim 3 , wherein the pH is in the range of from about 12 to about 13.
10. A method of cleaning a phosphorous-poisoned SCR catalyst, the method comprising cleaning the phosphorous-poisoned catalyst with an alkali metal hydroxide by immersing the catalyst in a soaking bath, an ultrasonic treatment solution, or a combination thereof, wherein the soaking bath or ultrasonic treatment solution has a pH in a range of from about 10 to about 14 and a temperature in the range from about 60° F. to about 140° F.
11. The method according to claim 10 , wherein the alkali metal hydroxide is sodium hydroxide, potassium hydroxide, or a combination thereof.
12. The method according to claim 10 , wherein the temperature of the soaking bath or treatment solution is in a range of from about 120° F. to about 130° F.
13. The method according to claim 10 , wherein the soaking bath or ultrasonic treatment further comprises a surface active substance.
14. The method according to claim 10 , wherein the concentration of alkali metal hydroxide is from about 0.1 weight % to about 4 weight %.