Refractory article and production process thereof
The present invention relates to refractory articles in general having improved surface properties. The objective of the invention is to propose an improvement of the refractory articles comprised of a fused silica matrix which will overcome the some of the defects while keeping the excellent known properties of the fused silica matrix. This objective is reached when a sintered ceramic phase is present in the porosity of at least a portion of at least a surface of the matrix. The present invention also relates to a process for producing such an article.
1. Refractory article consisting essentially of a fused silica matrix having a core and at least a surface, and a sintered ceramic phase, wherein the sintered ceramic phase is present in the porosity of at least a portion of at least a surface of the matrix, wherein the surface of the fused silica matrix remains the surface of the article, and wherein the sintered ceramic phase is introduced into a fused silica matrix comprising pores having a size from and including 1 micrometer to and including 0.1 micrometer.
2. Refractory article according to claim 1 , wherein the sintered ceramic phase is present up to a depth of between 200 μm and 1 mm from a surface of the matrix.
3. Refractory article according to claim 1 , wherein the sintered ceramic phase is present up to a depth of 500 μm from a surface of the matrix.
4. Refractory article according to claim 1 , wherein at least a portion of the surface of the matrix has a density higher than the density of the core of the matrix and a porosity lower than the porosity of the core of the matrix.
5. Refractory article according to claim 1 , wherein the sintered ceramic phase is selected from the group consisting of silicon, aluminum, zirconium and magnesium oxides, combinations thereof, boron, aluminum and silicon nitrides and combinations thereof, and aluminum and silicon oxynitrides and combinations thereof.
6. Refractory article according to claim 1 , wherein the refractory article comprises a roll for conveying hot articles, wherein the roll comprises a surface for conveying hot articles, and wherein the sintered ceramic phase is present in the portion of the surface contacting the article to be conveyed.
7. Refractory article according to claim 1 , wherein the refractory article comprises a crucible for handling or treating molten metal, wherein the crucible comprises an inner surface, and wherein the sintered ceramic phase is present in the inner surface of the crucible.