Grouting material
A grouting material which contains a fine particle material having a Blaine specific surface area of 5000 cm 2 /g or more, containing 30 to 60% by mass of cement clinker, 40 to 70 % by mass of and blast-furnace slag and 0.5 to 3 parts by mass of gypsum in terms of SO 3 based on 100 parts by mass of the total amount of cement clinker and blast-furnace slag, and further contains (i) 4 to 8 parts by mass of calcium-aluminate-based rapid-hardening admixture, (ii) 0.05 to 0.2 parts by mass of setting retarder and (iii) 0.5 to 1.7 parts by mass of high-performance water-reducing agent, based on 100 parts by mass of the fine particle material.
1. A grouting material which comprises
a fine particle material having a Blaine specific surface area of 5000 cm 2 /g or more containing
greater than 40% by mass and 60% by mass or less of cement clinker,
40% by mass or more and less than 60% by mass of blast-furnace slag and
0.5 to 3 parts by mass of gypsum in terms of SO 3 based on 100 parts by mass of the total amount of cement clinker and blast-furnace slag,
and further comprises
(i) 4 to 8 parts by mass of calcium-aluminate-containing rapid-hardening admixture,
(ii) 0.05 to 0.2 parts by mass of setting retarder and
(iii) 0.5 to 1.7 parts by mass of high-performance water-reducing agent, based on 100 parts by mass of the fine particle material.
2. The grouting material according to claim 1 , wherein the (i) calcium-aluminate-containing rapid-hardening admixture contains 12CaO.7Al 2 O 3 .
3. The grouting material according to claim 2 , wherein the (i) calcium-aluminate-containing rapid-hardening admixture further contains anhydrite.
4. The grouting material according to claim 1 , wherein the (ii) setting retarder is oxycarboxylic acid or a salt thereof.
5. The grouting material according to claim 1 , wherein the (iii) high performance water reducing agent is a melamine sulfonic acid condensation product.
6. The grouting material according to claim 1 , wherein the (i) calcium-aluminate-containing rapid-hardening admixture contains 12CaO.7Al 2 O 3 and anhydrite, the (ii) setting retarder is sodium gluconate and the (iii) high performance water-reducing agent is a melamine sulfonic acid condensation product.
7. The grouting material according to claim 1 , wherein the fine particle material contains greater than 40% by mass and 55% by mass or less of cement clinker.