Porous carbon foam composites, applications, and processes of making
Processes for producing porous carbon foam composites and activated carbon/carbon (AC/C) composites from polyimide precursors, activated carbon powder, and optionally carbon fiber and other additives. The AC/C composites may be used for carbon electrodes in electrochemical capacitors.
1. A process for producing porous carbon foam composite, comprising the steps of:
preparing a polyimide precursor powder;
mixing the polyimide precursor powder with an additive or additives in the form of powder, fiber, or both, to form a mixture;
consolidating the mixture of unmelted polyimide precursor powder and the additive or additives; and
pyrolyzing the consolidated mixture in an inert atmosphere to produce the porous carbon foam composite;
wherein the polyimide precursor powder is formed by imidization of poly(amic acids).
2. The process of claim 1 , wherein the additive is selected from the group consisting of carbon, zeolite, graphite, silicon, silicon oxides, tin oxides, titanium oxides, vanadium oxides, metals, metal alloys, metal oxides, metal nitrides, metal carbides, metallic compounds, silicon-containing polymers, boron containing polymers, and phosphorus containing polymers, inorganic compounds and organic compounds, and mixtures and combinations thereof.
3. The process of claim 1 , wherein the additive is mixed with the polyimide precursor powder after imidization and before solvent removal to produce the mixture.
4. The process of claim 1 , wherein the additive is added in the solution of poly(amic acids) before imidization and solvent removal to produce the mixture.
5. The process of claim 1 , wherein the porous carbon foam composite is an activated carbon/carbon (AC/C) composite, and wherein the additive comprises activated carbon powder, carbon fiber, or a mixture thereof.
6. The process of claim 1 , wherein the mixture is compressed under pressure in the range of about 2,000 psi to about 13,000 psi.
7. The process of claim 1 , wherein pyrolysis is conducted in a temperature range of about 600° C. to about 3,500° C.
8. The process of claim 1 , wherein consolidation of the mixture is performed by contacting the mixture with a substrate with at least one surface of the consolidated mixture binding to the substrate.
9. The process of claim 8 , wherein the substrate comprises a solid plate, a woven metal mesh, a bed of solid particles, a woven fiber pad, and a non-woven fiber pad.
10. The process of claim 1 , wherein the porous carbon foam composite is monolithic, granular, or irregularly shaped.
11. The process of claim 1 , wherein a metallic compound is added during the preparation of the polyimide precursor powder or added to the mixture.
12. The process of claim 11 , wherein the porous carbon foam composite is an activated carbon/carbon (AC/C) composite, and wherein the additive comprises activated carbon powder, carbon fiber, or a mixture thereof.
13. The process of claim 11 , wherein the metallic compound comprises metals selected from the group consisting of: Ti, Zr, V, Nb, Cr, Mo, Mn, Fe, Ru, Co, Ni, Pd, Cu, Ag, Zn, Pb, Hf, W, Ba, Al, Pt, Si, P, As, Li, Ga, Sn, Bi, V, Li, Mg, Ca, Sr, B, In, Si, Ge, Sc, Y, and combinations thereof.