Use of MgO doped with a divalent or trivalent metal cation for removing arsenic from water
Systems and methods for use of magnesium hydroxide, either directly or through one or more precursors, doped with a divalent or trivalent metal cation, for removing arsenic from drinking water, including water distribution systems. In one embodiment, magnesium hydroxide, Mg(OH) 2 (a strong adsorbent for arsenic) doped with a divalent or trivalent metal cation is used to adsorb arsenic. The complex consisting of arsenic adsorbed on Mg(OH) 2 doped with a divalent or trivalent metal cation is subsequently removed from the water by conventional means, including filtration, settling, skimming, vortexing, centrifugation, magnetic separation, or other well-known separation systems. In another embodiment, magnesium oxide, MgO, is employed, which reacts with water to form Mg(OH) 2 . The resulting Mg(OH) 2 doped with a divalent or trivalent metal cation, then adsorbs arsenic, as set forth above. The method can also be used to treat human or animal poisoning with arsenic.
1. A method of reducing the concentration of arsenic in water, comprising:
a) adding magnesium hydroxide and a trivalent metal cation to the water;
b) adsorbing the arsenic to the magnesium hydroxide; and then
c) separating and removing the magnesium hydroxide with adsorbed arsenic from the water, thereby reducing the concentration of arsenic in the water to below an acceptable level;
wherein the trivalent metal cation is Al 3+ ; and
wherein the magnesium hydroxide is added by adding particles of MgO coated with Al.
2. The method of claim 1 , wherein the magnesium hydroxide is added to the water at a magnesium hydroxide concentration of between 0.1 g/L and 0.5 g/L.
3. The method of claim 1 , wherein the trivalent cation is added to the water at a trivalent concentration of between 0.001 g/L and 0.1 g/L.
4. The method of claim 1 , wherein the magnesium hydroxide concentration added to the water is about 0.2 g/L; and the trivalent cation concentration added to the water is about 0.01 g/L.
5. The method of claim 1 , wherein the magnesium hydroxide comprises particles having a medium particle size less than 3 microns.
6. The method of claim 1 , wherein the magnesium hydroxide comprises particles having a medium particle size of about 0.5 microns.
7. The method of claim 1 , wherein the trivalent metal cation is added in the form of a metal salt, independently from adding magnesium hydroxide.
8. The method of claim 1 , wherein the magnesium hydroxide is added to the water by adding particles of magnesium oxide to the water, the magnesium oxide converting to magnesium hydroxide upon contact with the water.
9. The method of claim 1 , wherein the Al comprises about 5% of the mass of the particles of MgO coated with Al.
10. The method of claim 1 , wherein the magnesium hydroxide is disposed on the surface of a carrier particle.
11. The method of claim 10 , wherein the carrier particle is lighter than water and comprises a plastic or polystyrene microsphere.
12. The method of claim 10 , wherein the carrier particle is heavier than water and is selected from the group consisting of a sand particle, a glass microsphere, and a magnetic material.
13. A method of reducing the concentration of arsenic in water to below an acceptable level, comprising:
a) adding magnesium hydroxide and a trivalent metal cation to the water;
b) adsorbing the arsenic to the magnesium hydroxide; and then
c) separating and removing the magnesium hydroxide with adsorbed arsenic from the water, thereby reducing arsenic concentration in the water;
wherein the magnesium hydroxide is added to the water at a magnesium hydroxide concentration of about 0.2 g/L; and the trivalent cation is added to the water at a trivalent cation concentration of about 0.01 g/L; and
wherein the trivalent cation is aluminum cation; and
wherein the magnesium hydroxide comprises magnesium hydroxide particles having a medium particle size less than 3 microns; and
wherein the trivalent metal cation is added as a metal salt; and
wherein the magnesium hydroxide is added by adding particles of MgO coated with Al.