Hybrid grain boundary additives
View Patent ↗Magnetic layers are described that include the use of magnetic grains and non-magnetic grain boundaries with hybrid additives. Hybrid additives include the use of at least two different additives in the composition of the grain boundaries of a magnetic layer in magnetic recording media. The use of hybrid additives in the grain boundaries results in improved recording media. Methods for forming magnetic layers and magnetic recording media with the hybrid additive grain boundaries are also described.
1. An apparatus comprising:
a substrate;
one or more underlayers; and
a magnetic layer,
wherein the magnetic layer comprises magnetic grains and grain boundaries comprising hybrid additives, the hybrid additives having been formed by a combination of two different additives,
wherein a first of the two different additives is MgO, which imparts an undesired mixed c-axis orientation to the magnetic layer; and
wherein a second of the two different additives is C, with a ratio of MgO to C of about 50:50 by volume, to counteract the undesirable mixed c-axis orientation imparted to the magnetic layer by MgO.
2. An apparatus comprising:
a substrate;
one or more underlayers; and
a magnetic layer,
wherein the magnetic layer comprises magnetic grains and grain boundaries comprising hybrid additives, the hybrid additives having been formed by a combination of two different additives, and
wherein a first of the two different additives is C, which imparts an undesired increased
surface roughness to the magnetic layer, and
wherein a second of the two different additives is BN, with a ratio of BN to C of about 50:50 by volume, to counteract the undesirable increased surface roughness imparted to the magnetic layer by C.
3. An apparatus comprising:
a substrate;
one or more underlayers; and
a magnetic layer,
wherein the magnetic layer comprises magnetic grains and grain boundaries comprising hybrid additives, the hybrid additives having been formed by a combination of two different additives,
wherein a first of the two different additives is MgO that imparts an undesired mixed c-axis orientation to the magnetic layer, the MgO is in a range of about 5% to 95% by volume of the hybrid additive; and
wherein a second of the two different additives is C to counteract the undesirable mixed c-axis orientation imparted to the magnetic layer by MgO, the C is in a range of about 5% to 95% by volume of the hybrid additive.
4. The apparatus of claim 3 , wherein the MgO is in a range of about 20% to 80% by volume of the hybrid additive and wherein the C is in a range of about 20% to 80% by volume of the hybrid additive.
5. The apparatus of claim 3 , wherein the hybrid additive is between 10% and 70% by volume of the magnetic layer.
6. The apparatus of claim 5 , wherein the hybrid additive is between 30% and 50% by volume of the magnetic layer.
7. The apparatus of claim 3 wherein the magnetic layer comprises FePt or CoPt.
8. The apparatus of claim 3 and further comprising an overcoat layer over the magnetic layer.
9. The apparatus of claim 3 wherein a thickness of the magnetic layer is between about 5 nm and about 30 nm.
10. An apparatus comprising:
a substrate;
one or more underlayers; and
a magnetic layer,
wherein the magnetic layer comprises magnetic grains and grain boundaries comprising hybrid additives, the hybrid additives having been formed by a combination of two different additives,
wherein a first of the two different additives is C that imparts an undesired increased surface roughness to the magnetic layer, the C is in a range of about 5% to 95% by volume of the hybrid additive; and
wherein a second of the two different additives is BN to counteract the undesirable increased surface roughness imparted to the magnetic layer by C, the BN is in a range of about 5% to 95% by volume of the hybrid additive.
11. The apparatus of claim 10 , wherein the BN is in a range of about 20% to 80% by volume of the hybrid additive and wherein the C is in a range of about 20% to 80% by volume of the hybrid additive.
12. The apparatus of claim 11 , wherein the hybrid additive is between 10% and 70% by volume of the magnetic layer.
13. The apparatus of claim 12 , wherein the hybrid additive is between 30% and 50% by volume of the magnetic layer.
14. The apparatus of claim 10 wherein the magnetic layer comprises FePt or CoPt.
15. The apparatus of claim 10 and further comprising an overcoat layer over the magnetic layer.
16. The apparatus of claim 10 wherein a thickness of the magnetic layer is between about 5 nm and about 30 nm.