Method of impregnating crucibles and refractory articles
A method of sealing a surface and structure of a refractory crucible with a ceramic, comprising the steps of: (a) heating a refractory crucible to a predetermined temperature; (b) applying a wetting agent to a surface of the crucible; (c) applying a ceramic slip along the inner surface of the crucible; (d) applying a vacuum to an outer surface of the crucible; (e) removing excess slip from the inner surface of the crucible; (f) heating the crucible to remove moisture therefrom; and (g) firing the crucible at a temperature between 1,300° C. and about 1,700° C.
1. A method of sealing an inner surface of a refractory crucible with a ceramic, comprising the steps of:
(a) heating a refractory crucible to a temperature between about 100° C. and about 150° C., said crucible having an inner surface defining a material-containing cavity and an outer surface;
(b) applying a wetting agent to said inner surface of said crucible;
(c) applying a ceramic slip having a viscosity of about 100 to 3,500 centipoise along the surface of said crucible, said ceramic slip comprised of water, a wetting agent/dispersant and about 20% to 80% by weight of ceramic powder, at least 90% of said ceramic powder having a particle size of less than 1 micron said ceramic slip is applied to the inner surface of said crucible by filling said crucible with said ceramic slip;
(d) applying a vacuum to said crucible to draw said ceramic slip into the inner surface of said crucible;
(e) removing excess slip from the inner surface of said crucible;
(f) heating said crucible to remove moisture therefrom; and
(g) firing the crucible at a temperature between 1,300° C. and about 1,700° C. for about 2 to about 6 hours.
2. A method as defined in claim 1 , wherein said wetting agent is applied to said inner surface of said crucible by brushing.
3. A method as defined in claim 1 , wherein said wetting agent is applied to said inner surface of said crucible by spraying.
4. A method as defined in claim 1 , wherein said wetting agent is applied in a water solution including about 1% to about 3% by weight of a wetting agent or a dispersant.
5. A method as defined in claim 1 , wherein said vacuum is applied to said outer surface of said crucible by a vacuum chamber.
6. A method as defined in claim 5 , wherein a vacuum of at least 25 inches of mercury is applied to said crucible for about 5 to about 15 minutes.
7. A method as defined in claim 1 , wherein steps (b), (c) and (d) are repeated a plurality of times before said crucible is fired.
8. A method as defined in claim 1 , wherein said crucible is comprised of zirconia.
9. A method as defined in claim 1 , wherein said ceramic slip is comprised of ceramic powder selected from a group consisting of MgO—ZrO 2 , Y 2 O 3 —ZrO 2 , unstabilized ZrO 2 or combinations thereof.
10. A method of sealing a surface and structure of a refractory article with a ceramic, comprising the steps of:
(a) heating a refractory article to a temperature between about 100° C. and about 150° C.;
(b) applying a wetting agent to a surface of said article;
(c) applying a ceramic slip having a viscosity of about 100 to 3,500 centipoise along the surface of said article, said ceramic slip comprised of water, a wetting agent/dispersant and about 20% to 80% by weight of ceramic powder, at least 90% of said ceramic powder having a particle size of less than 1 micron;
(d) applying a vacuum to said article to draw said ceramic slip into the surface of said refractory article;
(e) removing excess slip from the surface of said refractory article;
(f) heating said article to remove moisture therefrom; and
(g) firing the article at a temperature between 1,300° C. and about 1,700° C. for about 2 to about 6 hours.
11. A method as defined in claim 10 , wherein said wetting agent is comprised of a water solution including about 1% to about 3% of a wetting agent or a dispersant.
12. A method as defined in claim 10 , wherein said vacuum is applied to said article by a vacuum chamber.
13. A method as defined in claim 12 , wherein a vacuum of at least 25 inches of mercury is applied to said article for about 5 to about 15 minutes.
14. A method as defined in claim 10 , wherein steps (b), (c) and (d) are repeated a plurality of times before said article is fired.
15. A method as defined in claim 10 , wherein said article is a crucible and said surface is an inner surface of said crucible.
16. A method as defined in claim 15 , wherein said crucible is comprised of zirconia.
17. A method as defined in claim 10 , wherein said ceramic slip is comprised of ceramic powder selected from a group consisting of MgO—ZrO 2 , Y 2 O 3 —ZrO 2 , unstabilized ZrO 2 , CrO 2 , Al 2 O 3 , or combinations thereof.