Method of forming opaque layer, recording process, ink set, ink cartridge, and recording apparatus
A method of forming an opaque layer includes forming a first layer by discharging droplets of an ink composition containing a metallic pigment on a record medium by an ink-jet recording process and forming a second layer by discharging droplets of an ink composition containing a white pigment on the record medium by an ink-jet recording process. The opaque layer is formed on the record medium on the side where the first layer and the second layer are formed in a region where the first layer and the second layer overlap each other.
1. A method of forming a composite layer comprising:
forming a first layer by discharging droplets of an ink composition containing a single pigment consisting of aluminum or aluminum alloy to a record medium by an ink-jet recording process;
forming a second layer by discharging droplets of an ink composition containing a single pigment consisting of white metal oxide particles to the record medium by an ink-jet recording process;
recording an image to the composite layer by an ink-jet recording process; and
heating the record medium during at least forming the first layer and forming the second layer;
wherein an average particle diameter of the metal oxide particles is 0.05 to 0.8 μm;
the aluminum or aluminum alloy pigment comprises plate-like particles, wherein when a major axis and a minor axis of flat surfaces of the plate-like particles are defined as X and Y respectively and a thickness of the particles is defined as Z, then a 50% average particle diameter of R50 based on circle-equivalent diameters determined form an X-Y plane area of the plate-like particles satisfies a condition: R50/Z>5, and R50 is in the range of 0.5 to 3 μm; and
a thickness of the first layer is 0.01 to 10 μm, and a thickness of the second layer is 0.1 to 10 μm; and
wherein an absolute value of difference (ΔL*) is not more than 1.5 according to the following expression:
ΔL*=(L1*value of a sample placed on a white medium (L*=93.6))−(L2*value of a sample placed on a black medium (L*=4.6)); and
wherein the sample(s) are formed by forming the first layer on the second layer on a surface of the record medium; and
wherein the second layer L2* value is not more than 49.8.
2. The method of forming a composite layer according to claim 1 , wherein
the first layer is closer to the record medium than the second layer is.
3. The method of forming a composite layer according to claim 2 , further comprising:
forming a third layer with an ink composition containing a metallic pigment on the second layer such that the second layer is between the third layer and the record medium.
4. The method of forming a composite layer according to claim 3 , further comprising:
forming a fourth layer with an ink composition containing a white pigment on the first layer such that the first layer is between the fourth layer and the record medium.
5. The method of forming an a composite according to claim 1 , wherein
the second layer is closer to the record medium than the first layer is.
6. The method of forming a composite layer according to claim 1 , wherein
the record medium is one selected from the group consisting of colorless transparent, translucent, colored transparent, colored translucent, chromatic opaque, and achromatic opaque objects.
7. The method of forming a composite layer according to claim 1 , wherein
the record medium has an image formed thereon.
8. The method of forming a composite layer according to claim 1 , wherein
the opaque layer has an L* value of 55 or higher.
9. The method of forming a composite layer according to claim 1 , wherein a thickness of the composite layer is at least 0.5 μm.
10. A recording process comprising carrying out the method of forming a composite layer according to claim 1 , and forming an image on the composite layer.