Process for manufacturing electrosurgical forceps with composite material tips
An electrosurgical forceps has at least the tip of one blade member formed of a composite material having aligned elongated particles of nickel interspersed in a matrix of silver particles. The tip can be provided as a tip member attached, such as by brazing, to the body of the blade member, or the entire blade member can be formed of the silver/nickel composite material. In another embodiment, the tip or blade member is formed of a dispersion strengthened silver or copper composite material.
1. A process for manufacturing electrosurgical forceps comprising:
blending a powder of silver particles and a powder of nickel particles to form a powder blend, the nickel content ranging from 5 weight percent to 40 weight percent, the balance comprising silver;
compacting and sintering the powder blend to form a sintered body;
extruding the sintered body to elongate and align particles of the nickel in a matrix of the silver;
forming a blade member or a tip member from the extrusion;
forming the blade member or the tip member into a first electrosurgical forceps blade;
providing a second electrosurgical forceps blade;
connecting the first electrosurgical blade and the second electrosurgical blade to electrodes at a connection; and
fixing the connection between the first electrosurgical blade, the second electrosurgical blade, and the electrodes within an insulating cap portion.
2. The process of claim 1 , further comprising aligning the elongated nickel particles with a longitudinal axis of the electrosurgical forceps blade.
3. The process of claim 1 , wherein the second electrosurgical forceps blade comprises at least a tip comprised of a composite material comprising aligned elongated particles of nickel interspersed in a matrix of silver particles.
4. The process of claim 1 , wherein the nickel content is 10 weight percent.