Low temperature polymer bonding using UV/ozone surface treatment
The present invention relates to a method for bonding two surfaces to one another. The invention particularly pertains to the use of such method in which one of the surfaces is a polymeric plastic (and more preferably a polymeric thermoplastic (especially poly-(methyl methacrylate) (“PMMA”) or cyclic olefin copolymer (“COC”)). More particularly, the invention relates to treating at least one of the contacting surfaces with UV in the presence of oxygen to thereby generate ozone (O 3 ) and atomic oxygen under conditions of temperature below that of the glass transition temperature of the polymeric plastic. The UV/O 3 -mediated bonding results in high bond strength and zero-deformation method. This bonding method can be applied to micro/nano-scale polymer devices, and particularly to microfluidic devices, for a low cost, high throughput, high yield advantage.
1. A method for bonding a first surface of a polymeric plastic to a second surface, wherein said method comprises:
(A) treating at least one of said surfaces with short wavelength UV light and in the presence of oxygen gas under conditions sufficient to generate a controlled concentration of oxygen and oxygen radicals;
(B) permitting said generated oxygen radicals to oxidize said at least one of said surfaces; and
(C) contacting said surfaces together to thereby bond them to one another, wherein bonding occurs at a temperature below a glass transition temperature of said surfaces.
2. The method of claim 1 , wherein both said first and said second surfaces are treated with said UV light.
3. The method of claim 1 , wherein said polymeric plastic is a polymeric thermoplastic and said step of treating is below the glass transition temperature of said polymeric thermoplastic.
4. The method of claim 1 , wherein both said first and said second surfaces are surfaces of polymeric thermoplastic.
5. The method of claim 4 , wherein the polymeric plastic of both said first and said second surfaces is the same polymeric thermoplastic.
6. The method of claim 3 wherein said polymeric thermoplastic is poly-(methyl methacrylate).
7. The method of claim 6 , wherein said temperature is from about 25° C. to about 95° C.
8. The method of claim 3 , wherein said polymeric thermoplastic is cyclic olefin copolymer.
9. The method of claim 8 , wherein said temperature is from about 25° C. to about 100° C.
10. A substrate comprising a thermoplastic polymer having a first surface bonded to a contacting second surface, wherein said bonding was accomplished through a method which comprises:
(A) treating said first or second surface with short wavelength UV light and in the presence of oxygen gas under conditions sufficient to generate a controlled concentration of oxygen and oxygen radicals; and
(B) permitting said generated oxygen radicals to oxidize said first or second surface, and thereby facilitate the bonding of said first surface to said second surface, wherein bonding occurs at a temperature below a glass transition temperature of said first and second surfaces;
wherein the bond between said surfaces is at least 10 fold greater than the maximal bond strength exhibited between said surfaces in the absence of said UV treatment.
11. The substrate of claim 10 , wherein the bond between said surfaces is at least 100 fold greater than the maximal bond strength exhibited between said surfaces in the absence of said UV treatment.
12. The substrate of claim 10 , wherein both said first and second surfaces are treated with said UV light.
13. The substrate of claim 10 , wherein both said first and said second surfaces are surfaces of polymeric thermoplastic.
14. The substrate of claim 13 , wherein the polymeric thermoplastic of both said first and said second surfaces is the same polymeric thermoplastic.
15. The substrate of claim 10 , wherein said polymeric thermoplastic is poly-(methyl methacrylate).
16. The substrate of claim 15 , wherein said bond strength is greater than 300 mJ/cm 2 .
17. The substrate of claim 10 , wherein said polymeric thermoplastic is cyclic olefin copolymer.
18. The substrate of claim 17 , wherein said bond strength is greater than 50 mJ/cm 2 .
19. The substrate of claim 10 , wherein said substrate is a microfluidic system comprising an interconnected reservoir and microchannel.
20. The substrate of claim 19 , wherein said microfluidic system conducts a preparative or analytical chemical reaction.
21. The method of claim 1 , wherein the concentration of oxygen within said surface increases by at least about 50% during said step of permitting said generated oxygen radicals to oxidize said bonding surface.