Functionally graded biocompatible coating and coated implant
The present invention provides a biocompatible coating comprising calcium phosphate that is functionally graded across the thickness of the coating. The coating, which preferably includes hydroxyapatite, is particularly useful for coating implants, such as dental or orthopedic implants. The functionally graded coating is generally crystalline near the interface with the surface of the implant, with crystallinity and crystal diameter decreasing toward the outer layer of the coating. The invention further provides methods for preparing a coated implant comprising a functionally graded calcium phosphate coating thereon. Furthermore, an antimicrobial agent can be dispersed within the calcium phosphate coating at discrete locations to provide for a coating with tailored release of the antimicrobial agent.
1. A biocompatible coating layer comprising a biphasic calcium phosphate material of a defined thickness, the coating layer having a first surface and a second, opposing surface, wherein the biphasic calcium phosphate material is functionally graded such that a higher percentage of the calcium phosphate at the first surface is amorphous and a higher percentage of the calcium phosphate at the second surface is crystalline, and wherein the coating layer comprises an antimicrobial agent dispersed within the thickness of the coating layer.
2. The biocompatible coating layer of claim 1 , wherein said calcium phosphate is selected from the group consisting of hydroxyapatite, tricalcium phosphate, and mixtures thereof.
3. The biocompatible coating layer of claim 1 , wherein the percentage of amorphous calcium phosphate at the first surface of the layer is at least 50%.
4. The biocompatible coating layer of claim 3 , wherein the percentage of amorphous calcium phosphate at the second surface of the layer is at least 75%.
5. The biocompatible coating layer of claim 1 , wherein the calcium phosphate at the second surface comprises crystalline calcium phosphate having crystals with a diameter in the range of about 2 nm to about 50 nm.
6. The biocompatible coating layer of claim 1 , wherein the antimicrobial agent is evenly dispersed within the thickness of the coating layer.
7. The biocompatible coating layer of claim 1 , wherein the antimicrobial agent dispersed within the coating layer is controllably released from the coating layer.
8. The biocompatible coating layer of claim 1 , wherein the antimicrobial agent is an elemental metal or metal alloy
9. The biocompatible coating layer of claim 1 , wherein the antimicrobial agent is a silver compound.
10. The biocompatible coating layer of claim 1 , wherein the antimicrobial agent is silver or a silver-platinum combination.
11. The biocompatible coating layer of claim 9 , wherein the silver compound is silver sulfadiazine.
12. The biocompatible coating layer of claim 1 , wherein the antimicrobial agent is an organic compound that exhibits antimicrobial activity.
13. The biocompatible coating layer of claim 1 , wherein the concentration of the antimicrobial agent is between about 0.1 and about 20 weight percent.
14. A biocompatible coated substrate comprising; a) a substrate having a surface; and b) a calcium phosphate coating having a defined thickness overlying at least a portion of the substrate surface and bonded thereto, the coating layer comprising an antimicrobial agent dispersed within the thickness of the coating layer, wherein the calcium phosphate is functionally graded such that an area of the coating proximal to the substrate is predominantly crystalline and an area of the coating distal to the substrate is predominantly amorphous.
15. The coated substrate of claim 14 , wherein said substrate is a prosthetic implant.
16. The coated substrate of claim 15 , wherein said prosthetic implant is selected from the group consisting of a dental implant and an orthopedic implant.
17. The coated substrate of claim 14 , wherein said substrate comprises one or more metallic materials.
18. The coated substrate of claim 14 , wherein said substrate comprises a polymeric material.
19. The coated substrate of claim 14 , wherein said coating layer has a thickness of about 100 nm to about 2,000 nm.
20. The coated substrate of claim 14 , wherein said coating layer has a thickness of about 200 nm to about 1,500 nm.
21. The coated substrate of claim 14 , wherein said calcium phosphate is selected from the group consisting of hydroxyapatite, tricalciumphosphate, and mixtures thereof.
22. The coated substrate of claim 14 , wherein the antimicrobial agent is evenly dispersed within the thickness of the coating layer.
23. The coated substrate of claim 14 , wherein the antimicrobial agent dispersed within the coating layer is controllably released from the coating layer.
24. The coated substrate of claim 14 , wherein the antimicrobial agent is an elemental metal or metal alloy.
25. The coated substrate of claim 14 , wherein the antimicrobial agent is silver or a silver-platinum combination.
26. The coated substrate of claim 14 , wherein the antimicrobial agent is a silver compound.
27. The coated substrate of claim 14 , wherein the silver compound is silver sulfadiazine.
28. The coated substrate of claim 14 , wherein the antimicrobial agent is an organic compound that exhibits antimicrobial activity.