Process for production of nickel and cobalt using metal hydroxide, metal oxide and/or metal carbonate
A method for producing metal oxide from a metal salt selected from nickel hydroxide, cobalt hydroxide, mixed nickel-cobalt hydroxide, nickel carbonate, cobalt carbonate or mixed nickel-cobalt carbonate includes providing a mixture of the metal salt, mixing the metal salt with a binder selected from an inorganic binder or an organic binder, forming the mixture into agglomerates, and calcining the agglomerates to produce metal oxide. Another method for making metallic nickel or cobalt includes providing the above metal salt, mixing the metal salt with the above binder to form a mixture, optionally adding water, forming the mixture into agglomerates, drying the agglomerates, adding an effective reducing amount of coke and/or coal and directly reducing the dried agglomerates with an effective amount of heat to produce metallic nickel and/or cobalt. Coke particles may be added to the mixture prior to agglomeration.
1. A method for making metallic nickel or cobalt comprising:
providing a metal salt selected from the group consisting of nickel hydroxide, cobalt hydroxide, mixed nickel-cobalt hydroxide, nickel carbonate, cobalt carbonate, mixed nickel-cobalt carbonate and combinations thereof;
blending the metal salt with a binder selected from the group consisting of inorganic binder and combinations of inorganic and organic binders, to form a mixture;
forming the mixture into agglomerates;
drying the agglomerates;
calcining the dried agglomerates to produce a metal oxide selected from the group consisting of nickel oxide, cobalt oxide and combinations thereof;
adding coke to the mixture; and
reducing the metal oxide to produce a metal selected from the group consisting of nickel, cobalt and combinations thereof.
2. The method for making metallic nickel or cobalt according to claim 1 further comprising adding water to the mixture.
3. The method for making metallic nickel or cobalt according to claim 1 , wherein the inorganic binder is selected from the group consisting of bentonite, quicklime, sodium silicate and combinations thereof.
4. The method for making metallic nickel or cobalt according to claim 1 wherein the organic binder is selected from the group consisting of lignin, guar gum, molasses, sugar, carboxymethylcellulose, cellulose, glycerol triacetate, polyethylene glycol, hydrolyzed starch, pregelatinized starch and combinations thereof.
5. The method for making metallic nickel or cobalt to claim 1 , wherein the binder is present in an amount ranging from about 2% to about 10% by weight.
6. The method for making metallic nickel or cobalt according to claim 1 , wherein the metal oxide is reduced by a gaseous reductant.
7. The method for making metallic nickel or cobalt according to claim 1 , wherein the metal oxide is reduced by coke or charcoal.
8. The method for making metallic nickel or cobalt according to claim 1 , further comprising adding flux to the metal, melting or smelting, and separating slag from the metal.
9. The method for making metallic nickel or cobalt according to claim 1 , wherein the agglomerates are dried at a temperature ranging from about 90° C. to about 110° C.
10. The method for making metallic nickel or cobalt according to claim 1 , wherein the agglomerates are calcined at a temperature ranging from about 1300° C. to about 1500° C.
11. The method for making metallic nickel or cobalt according to claim 1 , wherein the agglomerates are selected from the group consisting of pellets, briquettes, granules and extrudates.
12. The method of making metallic nickel or cobalt according to claim 1 , further comprising at least partially drying the metal salt prior to blending the metal salt with the inorganic binder.
13. The method of making metallic nickel or cobalt according to claim 1 , wherein the agglomerates are dried and calcined in one vessel.
14. A method for making metallic nickel or cobalt comprising:
providing a metal salt selected from the group consisting of nickel hydroxide, cobalt hydroxide, mixed nickel-cobalt hydroxide, nickel carbonate, cobalt carbonate and combinations thereof;
mixing the metal salt with a binder selected from the group consisting of inorganic binder and combinations of inorganic and organic binders, to form a mixture;
optionally adding water;
forming the mixture into agglomerates;
drying the agglomerates;
adding an effective reducing amount of a reducing agent selected from the group consisting of a gaseous reductant, coke, charcoal and combinations thereof;
adding coke to the mixture; and
directly reducing the dried agglomerates with an effective amount of heat to produce a metal selected from the group consisting of nickel, cobalt and combinations thereof.
15. The method for making metallic nickel or cobalt according to claim 14 wherein the inorganic binder is selected from the group consisting of bentonite, quicklime, sodium silicate and combinations thereof.
16. The method for making metallic nickel or cobalt according to claim 14 wherein the organic binder is selected from the group consisting of lignin, guar gum, molasses, sugar, carboxymethylcellulose, cellulose, glycerol triacetate, polyethylene glycol, hydrolyzed starch, pregelatinized starch and combinations thereof.
17. The method for making metallic nickel or cobalt according to claim 14 , wherein the binder is present in an amount ranging from about 2% to about 10% by weight.
18. The method for making metallic nickel or cobalt according to claim 14 wherein the dried agglomerates are reduced by a gaseous reductant.
19. The method for making metallic nickel or cobalt according to claim 14 wherein the dried agglomerates are reduced by coke or charcoal.
20. The method for making metallic nickel or cobalt according to claim 14 , further comprising adding flux to the metal; melting or smelting; and separating slag from the metal.
21. The method for making metallic nickel or cobalt according to claim 14 , wherein the agglomerates are dried at a temperature ranging from about 90° C. to about 110° C.
22. The method for making metallic nickel or cobalt according to claim 14 , wherein the agglomerates are selected from the group consisting of pellets, briquettes, granules and extrudates.
23. The method for making metallic nickel or cobalt according to claim 14 , further comprising at least partially drying the metal salt prior to blending the metal salt with the inorganic binder.
24. The method for making metallic nickel or cobalt according to claim 14 , wherein the agglomerates are dried and reduced in one vessel.
25. A method for making metallic nickel or cobalt comprising
providing a metal salt selected from the group consisting of nickel hydroxide, cobalt hydroxide, mixed nickel-cobalt hydroxide, nickel carbonate, cobalt carbonate and combinations thereof;
mixing the metal salt with a binder selected from the group consisting of inorganic binder, organic binder and combinations thereof;
mixing the metal salt and binder with coke particles to form a mixture;
optionally adding water;
forming the mixture into agglomerates;
drying the agglomerates,
adding an effective reducing amount of coke and/or coal to the dried agglomerates, and
directly reducing the dried agglomerates with an effective amount of heat to produce a metal selected from the group consisting of nickel, cobalt and combinations thereof.
26. The method for making metallic nickel or cobalt according to claim 15 wherein the inorganic binder is selected from the group consisting of bentonite, quicklime, sodium silicate and combinations thereof.
27. The method for making metallic nickel or cobalt according to claim 15 wherein the organic binder is selected from the group consisting of lignin, guar gum, molasses, sugar, carboxymethylcellulose, cellulose, glycerol triacetate, polyethylene glycol, hydrolyzed starch, pregelatinized starch and combinations thereof.
28. The method for making metallic nickel or cobalt according to claim 15 , wherein the binder is present in an amount ranging from about 2% to about 10% by weight.
29. The method for making metallic nickel or cobalt according to claim 15 further comprising subjecting the dried agglomerates to a gaseous reductant.
30. The method for making metallic nickel or cobalt according to claim 15 , further comprising adding flux to the metal; melting or smelting; and separating slag from the metal.
31. The method for making metallic nickel or cobalt according to claim 15 , wherein the agglomerates are dried at a temperature ranging from about 90° C. to about 110° C.
32. The method for making metallic nickel or cobalt according to claim 15 , wherein the agglomerates are selected from the group consisting of pellets, briquettes, granules and extrudates.
33. The method for making metallic nickel or cobalt according to claim 25 , further comprising at least partially drying the metal salt prior to blending the metal salt with the inorganic binder.
34. The method for making metallic nickel or cobalt according to claim 25 , wherein the agglomerates are dried and reduced in one vessel.