METHOD FOR MANUFACTURING MAGNETIC SHEET AND MAGNETIC SHEET
In manufacturing a magnetic sheet, the magnetic sheet is formed by applying on a prescribed substrate a magnetic paint made from a mixture of at least flat soft magnetic powder and polymeric binder dissolved in a solvent and drying the magnetic paint. Subsequently, the magnetic paint is further coated on the magnetic sheet formed by drying the magnetic paint and is dried. Thus, an extremely high quality magnetic sheet is made with high productivity.
1 . A method for manufacturing a magnetic sheet comprising the steps of:
coating, on a predetermined substrate, a magnetic paint made from a mixture of an at least flat soft magnetic powder and a polymeric binder dissolved in a solvent and drying the magnetic paint to form a magnetic sheet; and
further coating and drying the magnetic paint on the magnetic sheet dried to be formed.
2 . The method for manufacturing the magnetic sheet according to claim 1 , wherein the drying step is so made that a containing amount of the solvent is equal to or less than one percent.
3 . The method for manufacturing the magnetic sheet according to claim 1 , wherein the magnetic paint includes a cross-linking agent, and wherein a drying temperature of the magnetic paint after coating is lower than a temperature of cross-linking starting temperature of the cross-linking agent.
4 . The method for manufacturing the magnetic sheet according to any one of claims 1 to 3 , wherein the magnetic paint includes a cross-linking agent, and wherein the method for manufacturing the magnetic sheet further comprising the steps of:
compressing the dried and formed magnetic sheet at a temperature equal to or higher than a glass transition temperature of the polymeric binder and lower than a reaction start temperature between the polymeric binder and the cross-linking agent; and
compressing the magnetic sheet at a temperature equal to or higher than the reaction start temperature between the polymeric binder and the cross-linking agent.
5 . The method for manufacturing the magnetic sheet according to any one of claims 1 to 3 , further comprises the step of compressing the dried and formed magnetic sheet.
6 . The method for manufacturing the magnetic sheet according to any one of claims 1 to 5 , wherein the magnetic paint includes dispersed particles added so as to disperse to the polymeric binder.
7 . The method for manufacturing the magnetic sheet according to claim 6 , wherein the dispersed particles are a flame retardant.
8 . A magnetic sheet comprising a magnetic paint made from a mixture of an at least flat soft magnetic powder and a polymeric binder dissolved in a solvent, wherein the magnetic sheet is made by coating and drying the magnetic paint on the magnetic sheet formed by drying the magnetic paint after coating the magnetic paint on a predetermined substrate.