Coating composition comprising calcium hydrogen-phosphate, processes for preparing it, its use and substrates coated with it
The abstract concerns a coating composition comprising 25-55% by weight of one or more film formers, 2.5-55% by weight of one or more fillers, 0-10% by weight of one or more additives, and 0-30% by weight of a solvent, based on the total weight of the coating composition. As the filler or a filler the composition comprises calcium hydrogen phosphate in a mass fraction of 2.5-20%, preferably 5-15%, more preferably 7.5-11% by weight based on the total weight of the coating composition. The invention further concerns processes for preparing this coating composition, its use as a coating material in the vehicle sector, and substrates produced therewith.
1. A coating composition comprising:
25-55% by weight of one or more film formers comprising a combination of at least one hydroxy-functional component, at least one aldimine and/or ketimine, and at least one polyisocyanate,
2.5-55% by weight of one or more fillers wherein at least one filler comprises calcium hydrogen phosphate in a mass fraction of 2.5 to 20% based on the total weight of the coating composition wherein the calcium hydrogen phosphate has an average particle size of 2.5 to 4.0 μm,
0-10% by weight of one or more additives, and
1-30% by weight of a solvent, based on the total weight of the coating composition, wherein the coating composition comprises less than 540 g/l volatile organic compounds (VOC).
2. The coating composition of claim 1 , wherein as film former a combination of at least one hydroxy-functional component, at least one ketimine, and at least one polyisocyanate is present.
3. The coating composition of claim 1 , wherein the at least one aldimine or ketimine comprises the reaction product of isophorone diamine with a corresponding aldehyde or ketone, respectively.
4. The coating composition of claim 1 , wherein the at least one polyisocyanate comprises a polyisocyanate based on at least one of hexamethylene diisocyanate, isophorone diisocyanate or trimethyl hexamethylene diisocyanate.
5. The coating composition of claim 4 , wherein the at least one polyisocyanate comprises a polyisocyanate based on an asymmetric hexamethylene diisocyanate trimer.
6. The coating composition of claim 1 , wherein the at least one hydroxy-functional component comprises a branched polyalcohol having ester groups, ether groups, or a combination thereof.
7. The coating composition of claim 1 , comprising less than 250 g/l volatile organic compounds (VOC).
8. The coating composition of claim 1 , further comprising one or more additives selected from the group consisting of dispersants, rheological additives, antisettling agents, pigment stabilizers, fillers, and ceramic microspheres.
9. A coating composition comprising:
25-55% by weight of one or more film formers comprising a combination of at least one hydroxy-functional component, at least one aldimine and/or ketimine, and at least one polyisocyanate,
2.5-55% by weight of one or more fillers wherein at least one filler comprises calcium hydrogen phosphate in a mass fraction of 7.5 to 11% based on the total weight of the coating composition wherein the calcium hydrogen phosphate has an average particle size of 2.5 to 4.0 μm,
0-10% by weight of one or more additives, and
1-30% by weight of a solvent, based on the total weight of the coating composition, wherein the coating composition comprises less than 540 g/l volatile organic compounds (VOC).
10. A coating composition comprising:
25-55% by weight of one or more film formers comprising a combination of at least one hydroxy-functional component, at least one aldimine and/or ketimine, and at least one polyisocyanate, wherein the at least one hydroxy-functional component comprises a branched polyalcohol having ester groups, ether groups, or a combination thereof,
2.5-55% by weight of one or more fillers wherein at least one filler comprises calcium hydrogen phosphate in a mass fraction of 7.5 to 11% based on the total weight of the coating composition wherein the calcium hydrogen phosphate has an average particle size of 2.5 to 4.0 μm,
0-10% by weight of one or more additives, and
1-30% by weight of a solvent, based on the total weight of the coating composition, wherein the coating composition comprises less than 540 g/l volatile organic compounds (VOC).
11. A coated substrate comprising: a coating, the coating being produced by a coating composition comprising
25-55% by weight of one or more film formers comprising a combination of at least one hydroxy-functional component, at least one aldimine and/or ketimine, and at least one polyisocyanate,
2.5-55% by weight of one or more fillers wherein at least one filler comprises calcium hydrogen phosphate in a mass fraction of 2.5 to 20% based on the total weight of the coating composition wherein the calcium hydrogen phosphate has an average particle size of 2.5 to 4.0 μm,
0-10% by weight of one or more additives, and
1-30% by weight of a solvent, based on the total weight of the coating composition, wherein the coating composition comprises less than 540 g/l volatile organic compounds (VOC); and
a substrate comprising aluminum.
12. A coated substrate comprising:
a coating, the coating being produced by a coating composition comprising
25-55% by weight of one or more film formers comprising a combination of at least one hydroxy-functional component, at least one aldimine and/or ketimine, and at least one polyisocyanate, wherein the at least one hydroxy-functional component comprises a branched polyalcohol having ester groups, ether groups, or a combination thereof,
2.5-55% by weight of one or more fillers wherein at least one filler comprises calcium hydrogen phosphate in a mass fraction of 7.5 to 11% based on the total weight of the coating composition wherein the calcium hydrogen phosphate has an average particle size of 2.5 to 4.0 μm,
0-10% by weight of one or more additives, and
1-30% by weight of a solvent, based on the total weight of the coating composition, wherein the coating composition comprises less than 540 g/l volatile organic compounds (VOC); and
a substrate comprising aluminum.
13. The coating composition of claim 1 , wherein the at least one filler comprises calcium hydrogen phosphate in a mass fraction of 7.5 to 20% based on the total weight of the coating composition.