Method for marking an item based on colour centres
View Patent ↗The invention relates to a method for marking an item based on the formation of color centers on a lithium fluoride film. The method provides for the deposition of thin LiF films on the item or on mark supports to be applied to the item and the formation of the color centers by irradiation, thus forming an identification mark. Optionally, the method may provide for the detection of the identification mark and the control of its authenticity. The method may be employed both to guarantee the authenticity of the item and to classify it. The application of the method is particularly advantageous in the field of high value goods and specifically in the field of cultural objects.
1. A method for marking an item comprising at least the steps of:
depositing by evaporation a lithium fluoride film having a thickness of at least 20 nm obtained by evaporating the same on the item or on a mark support to be applied to the item to be marked;
irradiating the previously obtained lithium fluoride film by means of a ionising radiation beam having an energy of at least 0.4 keV controlled by computerised means to carry out the desired identification mark,
wherein the depositing step is performed at an atmospheric pressure and in an atmosphere consisting of air or nitrogen.
2. The method according to claim 1 comprising the further step of:
detecting the presence of the identification mark obtained by illuminating the same by means of a light source emitting a blue-ultraviolet light.
3. The method according to claim 1 comprising the further steps of
detecting the presence of the identification mark obtained by illuminating the same by means of a light source emitting a blue-ultraviolet light;
controlling the authenticity of the identification mark by means of the measurement of the absorbance or emission spectrum of the same.
4. The method according to claim 1 , wherein the temperature of the item or of a mark support to be applied to the item during the steps of evaporation and irradiation is in a range comprised from 15° C. to 90° C.
5. The method according to claim 4 , wherein said temperature is 25° C.
6. The method according to claim 1 , wherein a lithium fluoride film having a thickness in the range from 20 to 200 nm is obtained by:
evaporating lithium fluoride at a flow rate in the range from 0.2 Å/s to 3 Å/s for a time in the range from 60 secs to 170 mins;
placing the item or the mark support at a distance in the range from 5 to 30 cm from the evaporator.
7. The method according to claim 6 , wherein the lithium fluoride film is obtained by:
evaporating lithium fluoride with a flow rate of 1 Å/s;
placing the item or the mark support at a distance of 8 cm from the evaporator.
8. The method according to claim 6 , wherein lithium fluoride has a granulometry in the range from 0.01 to 5 mm.
9. A method according to claim 8 , wherein lithium fluoride has a granulometry of 0.5-2 mm.
10. The method according to claim 1 , wherein the irradiation is obtained under vacuum conditions in the range from 5×10 −3 to 5×10 −7 mbars with a ionising radiation beam having an energy in the range from 1 to 5 keV emitted by an electronic cannon with an emission current in the range from 0.01 to 0.1 μA.
11. The method according to claim 10 , wherein the irradiation is obtained under vacuum conditions of <1×10 −4 mbars with a ionising radiation beam having an energy of 3 keV emitted by an electronic cannon with an emission current of 0.05 μA.
12. The method according to claim 10 , wherein the irradiation is obtained for a time in the range from 1 to 30 secs.
13. The method according to claim 10 , wherein the irradiation is obtained for a time of 10 secs.
14. The method according to claim 10 , wherein the ionising radiation beam spot has a size in the range from 200 nm to 2 mm.
15. The method according to claim 10 , wherein the ionising radiation beam spot has a size of 80 μm.
16. The method according to claim 1 , wherein the irradiation is obtained under vacuum conditions in the range from 1×10 −11 to 5×10 −6 mbars with a ionising radiation beam having an energy in the range from 0.4 to 1.2 keV with a density in the range from 10 17 to 10 20 photons/secs/cm 2 emitted by a synchrotron.
17. The method according to claim 16 , wherein the irradiation is obtained under vacuum conditions<10 −9 mbars with a ionising radiation beam having an energy of 0.65 keV with a density of 10 19 photons/secs/cm 2 emitted by a synchrotron.
18. The method according to claim 16 , wherein the irradiation time for each dot of the identification mark is in the range from 10 to 100 msecs.
19. The method according to claim 16 , wherein the irradiation time for each dot of the identification mark is 10 msecs.
20. The method according to claim 16 , wherein the ionising radiation beam has a the photon spot size in the range from 200 nm to 5 μm.
21. The method according to claim 2 , wherein the identification mark is detected by means of a fluorescence microscope.
22. The method according to claim 2 , wherein the identification mark is detected by means of an instrument emitting a light in the blue-ultraviolet region which illuminates the identification mark and an orange filter.