Particles comprising composite of para-aramid and additive material
The invention pertains to a method for making a polymer-additive composite particle from a dope by jet spinning the dope to obtain a pulp, fibril or fibrid, wherein the solvent of the dope is selected from N-methyl-2-pyrrolidone, N,N′-dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, and 4 to 75 wt % of a composition consisting of 2 to 95 wt % of a para-aramid polymer and 5-98 wt % of a solid additive material, to a total of 100 wt %, and wherein the aramid polymer is dissolved in the solvent; or coagulating the dope by means of a rotor-stator apparatus in which the polymer solution is applied through the stator on the rotor so that the precipitating polymer-additive composite particle is subjected to shear forces while they are in a plastic deformable stage.
1. A method for making a polymer-additive composite pulp, fibril or fibrid from a dope by:
i) jet spinning the dope through a jet spin nozzle to obtain the pulp, fibril or fibrid, the dope including (a) a solvent that is selected from the group consisting of N-methyl-2-pyrrolidone, N,N′-dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, and mixtures thereof; and (b) 4 to 75 wt % of a composition consisting of a para-aramid polymer and a solid additive, the para-aramid polymer being present in the composition in an amount of 2 to 80 wt % and the solid additive material being present in the composition in an amount of 20 to 98 wt %; wherein the para-aramid polymer is dissolved in the solvent; or
ii) coagulating the dope to obtain the pulp, fibril or fibrid by means of a rotor-stator apparatus, in which the dope is applied through the stator on the rotor so that polymer-additive composite pulp, fibril or fibrid are precipitated and subjected to shear forces while the polymer-additive composite pulp, fibril or fibrid are in a plastic deformable stage, wherein said pulp, fibril or fibrid comprises a para-aramid polymer and a solid additive, the dope including (a) a solvent that is selected from the group consisting of N-methyl-2-pyrrolidone, N,N′-dimethylformamide, N,N′-dimethylacetamide, tetra-methylurea, and mixtures thereof; and (b) 4 to 75 wt % of a composition consisting of a para-aramid polymer and a solid additive, the para-aramid polymer being present in the composition in an amount of 2 to 80 wt % and the solid additive material being present in the composition in an amount of 20 to 98 wt %; wherein the para-aramid polymer is dissolved in the solvent.
2. A method for making a polymer-additive material composite fibrid film from a dope by:
i) spinning the dope through a jet spin nozzle to obtain a polymer stream, the dope including (a) a solvent that is selected from the group consisting of N-methyl-2-pyrrolidone, N,N′-dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, and mixtures thereof; and (b) 4 to 75 wt. % of a composition consisting of a para-aramid polymer and a solid additive, the para-aramid polymer being present in the composition in an amount of 2 to 80 wt % and the solid additive material being present in the composition in an amount of 20 to 98 wt %; wherein the para-aramid polymer is dissolved in the solvent; and
ii) hitting the polymer stream with a coagulant at an angle wherein a vector of coagulant velocity perpendicular to the polymer stream is at least 5 m/s to coagulate the polymer stream and obtain the fibrid film.
3. The method according to claim 2 , wherein the vector of the coagulant velocity perpendicular to the polymer stream is at least 10 m/s.
4. A method for making a polymer-additive material composite pulp or fibril from a dope by:
i) converting the dope to pulp or fibrils by using a jet spin nozzle under a gas stream, the dope including (a) a solvent that is selected from the group consisting of N-methyl-2-pyrrolidone, N,N′-dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, and mixtures thereof; and (b) 4 to 75 wt. % of a composition consisting of a para-aramid polymer and a solid additive, the para-aramid polymer being present in the composition in an amount of 2 to 80 wt % and the solid additive material being present in the composition in an amount of 20 to 98 wt %; wherein the para-aramid polymer is dissolved in the solvent; and then
ii) coagulating the pulp or fibrils using a coagulation jet.