Method of pressureless sintering production of densified ceramic composites
View Patent ↗Methods of making and compositions of dense sintered ceramic nano- and micro-composite materials that are highly stable in a variety of conditions and exhibit superior toughness and strength. Liquid feed flame spray pyrolysis techniques form a plurality of nanoparticles (e.g., powder), each having a core region including a first metal oxide composition comprising Ce and/or Zr or other metals and a shell region including a second metal oxide composition comprising Al or other metals. In certain aspects, the core region comprises a partially stabilized tetragonal ZrO 2 and the shell region comprises an α-Al 2 O 3 phase. The average actual density of the ceramic after sintering is greater than 50% and up to or exceeding 90% of a theoretical density of the ceramic.
1. A method of making a dense ceramic nano- and/or micro-structured or ultrafine composite, the method comprising:
aerosolizing a liquid precursor stream with oxygen to form an aerosolized stream, wherein said liquid precursor stream comprises a first metal oxide precursor and a second metal oxide precursor distinct from said first metal oxide precursor; and
combusting said aerosolized stream to form a plurality of nanoparticles having an average particle size diameter of less than or equal to about 500 nm and defining a core region comprising a first oxide composition formed from said first metal oxide precursor and a shell region comprising a second oxide composition comprising aluminum or iron formed from said second metal oxide precursor, wherein the first oxide composition has a first bulk diffusion rate that is distinct from a second bulk diffusion rate of the second oxide composition;
forming a green body from said plurality of nanoparticles;
sintering said green body to form the ceramic composite having an average actual density of greater than or equal to about 90% of a theoretical density of the sintered ceramic composite.
2. The method of claim 1 , wherein the combusting further comprises forming nanoparticles having an average particle size diameter of less than or equal to about 500 nm and defining a core region comprising a first oxide composition formed from said first metal oxide precursor and a partial shell region comprising a second oxide composition formed from said second metal oxide precursor, wherein said first and second metal oxide precursors are incompletely reacted.
3. The method of claim 1 , wherein the first oxide composition has a first bulk diffusion rate that is lower than a second bulk diffusion rate of the second oxide composition.
4. The method of claim 1 , wherein said average actual density is greater than or equal to about 99% of said theoretical density of the sintered ceramic composite.
5. The method of claim 1 , wherein at least a portion of said second oxide composition undergoes a phase transformation prior to or during said sintering.
6. The method of claim 1 , wherein a ratio of the first oxide composition to the second oxide composition ranges from about 1:100 to about 100:1.
7. The method of claim 1 , wherein said first oxide composition comprises zirconium oxide (ZrO 2 ) and said second oxide composition comprises aluminum oxide (Al 2 O 3 ).
8. The method of claim 7 , wherein at least a portion of said zirconium oxide (ZrO 2 ) is a stable tetragonal-zirconium oxide phase.
9. The method of claim 8 , wherein at least a portion of said aluminum oxide (Al 2 O 3 ) comprises a δ-Al 2 O 3 phase prior to said combusting and/or said sintering that is transformed to an α-Al 2 O 3 phase after said sintering.
10. The method of claim 7 , wherein at least a portion of said zirconium oxide (ZrO 2 ) after said sintering comprises a stable tetragonal-zirconium oxide phase.
11. The method of claim 1 , wherein said first oxide composition comprises an element selected from the group consisting of: zirconium (Zr), cerium (Ce), magnesium (Mg), yttrium (Y), nickel (Ni), cobalt (Co), zinc (Zn), and mixtures thereof.
12. The method of claim 1 , further comprising mixing said aerosolized stream with a pre-formed particle prior to said combusting, wherein during said combusting said first metal oxide precursor and said second metal oxide precursor form a metal oxide coating on said pre-formed particle.
13. A method of making a dense ceramic nano and/or micro-structured ultrafine composite, the method comprising:
aerosolizing a liquid precursor stream with oxygen to form an aerosolized stream, wherein said liquid precursor stream comprises a first precursor comprising zirconium and a second precursor comprising aluminum;
combusting said aerosolized stream to form a plurality of nanoparticles having an average particle size diameter of less than or equal to about 500 nm, wherein each nanoparticle comprises a core region and a shell region disposed around said core region, where said core region comprises zirconium oxide (ZrO 2 ) and said shell region comprises aluminum oxide (Al 2 O 3 );
forming a green body comprising said plurality of nanoparticles;
sintering said green body to form the dense ceramic composite having an average actual density of greater than or equal to about 50% of a theoretical density of the sintered ceramic composite, wherein at least a portion of said aluminum oxide (Al 2 O 3 ) comprises a δ-Al 2 O 3 phase prior to or during said sintering that is transformed to an α-Al 2 O 3 phase after said sintering.
14. The method of claim 13 , further comprising quenching said aerosolized stream after said combusting to form said plurality of nanoparticles.
15. The method of claim 13 , further comprising a heating step before said sintering that burns off any residual surface or internal impurities present from said forming of said green body.
16. The method of claim 13 , wherein said sintering is conducted at a temperature and a pressure that minimizes grain growth and controls the phase transformation of α-alumina from a δ-alumina and prevents phase transformation of monoclinic zirconia phase to tetragonal zirconia phase.
17. The method of claim 13 , wherein at least a portion of said zirconium oxide (ZrO 2 ) is a stable tetragonal-zirconium oxide phase.
18. The method of claim 13 , wherein said average actual density is greater than or equal to about 99% of said theoretical density of the sintered ceramic composite.
19. The method of claim 13 , wherein a ratio of the zirconium oxide (ZrO 2 ) to the aluminum oxide (Al 2 O 3 ) ranges from about 1:100 to about 100:1.
20. A method of making a dense ceramic nano- and/or micro-structured or ultrafine composite, the method comprising:
aerosolizing a liquid precursor stream with oxygen to form an aerosolized stream, wherein said liquid precursor stream comprises a plurality of precursor nanoparticles and a metal oxide precursor; and
combusting said aerosolized stream to form a plurality of coated nanoparticles having an average particle size diameter of less than or equal to about 500 nm and defining a core region comprising at least one of said precursor nanoparticles and a shell region comprising an oxide composition formed from said metal oxide precursor;
forming a green body from said plurality of coated nanoparticles;
sintering said green body to form the ceramic composite having an average actual density of greater than or equal to about 90% of a theoretical density of the sintered ceramic composite.
21. The method of claim 20 , wherein the precursor nanoparticles comprise a core region comprising a first metal oxide composition comprising at least one element selected from the group consisting of: zirconium (Zr), cerium (Ce), aluminum (Al), magnesium (Mg), yttrium (Y), nickel (Ni), cobalt (Co), zinc (Zn), iron (Fe), and mixtures thereof, and a shell region comprising a second metal oxide composition comprising aluminum oxide (Al 2 O 3 ).
22. The method of claim 21 , wherein said first metal oxide composition comprises cerium oxide (CeO 2 ), zirconium oxide (ZrO 2 ), cerium zirconium oxide (CeZrO 2 ), spinel or magnesium aluminate (MgAl 2 O 4 ) and/or yttrium aluminate garnet (Y 3 Al 5 O 12 ).
23. The method of claim 21 , wherein said first metal oxide composition comprises zirconium oxide (ZrO 2 ) in a partially stabilized tetragonal phase (t-ZrO 2 ).
24. The method of claim 21 , wherein said second metal oxide composition comprises said aluminum oxide in an alpha phase (α-Al 2 O 3 ).