Method for producing implants with an ultrahydrophilic surface
The present invention concerns a process for the production of implants with an ultrahydrophilic surface as well as the implants produced in that way and also processes for the production of loaded, so-called bioactive implant surfaces of metallic or ceramic materials, which are used for implants such as artificial bones, joints, dental implants or also very small implants, for example what are referred to as stents, as well as implants which are further produced in accordance with the processes and which as so-called “delivery devices” allow controlled liberation, for example by way of dissociation, of the bioactive molecules from the implant materials.
1. A process for the production of an implant with an ultrahydrophilic surface with dynamic contact angles from 0° to 10° upon wetting of the surface of the implant with water, comprising the steps of:
(a) providing a metal implant having a surface made from a material selected from the group consisting of a metal, a metal alloy, and a combination of a ceramic material with a metal or metal alloy;
(b) immersing the metal implant in chromosulphuric acid having a density of more than 1.40 g/cm 3 , at a temperature of above 200° C., for a period of from 10 to 90 minutes; and
(c) directly after removal, quenching the metal implant by immersion in concentrated sulphuric acid at a temperature of 15° to 25° C. and washing the surface of the metal implant with distilled water in a plurality of washing steps.
2. A process according to claim 1 in which step (b) is carried out until the dynamic contact angles are in a region of a minimum in a diagram upon plotting of the dynamic contact angle against the time duration of step (b).
3. A process according to claim 1 comprising the further step of treating said surface with an aqueous solution of a chelating agent.