Polyethylene naphthalate fiber and method for producing the same
The polyethylene naphthalate fiber for industrial material having a low fatigue in a composite is a polyethylene naphthalate fiber for industrial material containing an ethylene-2,6-naphthalate unit in 80% or more, characterize by having a strength of 6 cN/dtex or more and a secondary yield point elongation degree of 8% or less. The production method thereof is a method for producing a fiber in which a fiber having been obtained by melt-spinning a polyethylene naphthalate is subjected to stretching, characterized in that prestretch satisfying such conditions as the fiber temperature of from 80° C. to 120° C. and from 0.05 to 0.3 N/dtex is performed, a first stretch satisfying such conditions as the fiber temperature of from 130° C. to 180° C. and stretch tensile force of not more than the prestretch tensile force is performed, the total stretch magnification including subsequent stretches is set to 5 or more, and finally heat-treatment under tension with a stretch ratio of from 0 to 2% is performed.
1. A polyethylene naphthalate fiber comprising an ethylene-2,6-naphthalate unit in 80% or more, wherein the polyethylene naphthalate fiber has a strength of 6 cN/dtex or more, a secondary yield point elongation degree of 8% or less, a rupture elongation degree is from 11 to 20%, a difference between the secondary yield point elongation degree and the rupture elongation degree is from 4 to 10%, and a terminal modulus, which is the difference between the rupture stress and a stress at an elongation degree before the rupture by 1%, of from 0.1 to 0.5 cN/dtex.
2. The polyethylene naphthalate fiber according to claim 1 wherein the intermediate load elongation degree at 4.0 cN/dtex is from 2 to 4%.
3. The polyethylene naphthalate fiber according to claim 1 , wherein the thermal contraction ratio at 180° C. is from 3 to 7%.
4. A method for producing a polyethylene naphthalate fiber in which a fiber having been obtained by melt-spinning a polyethylene naphthalate containing an ethylene-2,6-naphthalate unit in 80% or more is subjected to multistage stretching without once being wound,
wherein
the temperature of the takeoff roller is in the range of from 85 to 130°, prestretch satisfying such conditions as the fiber temperature of from 80° C. to 120° C., and the prestretch tensile force of from 0.5 to 3.0 cN/dtex and the prestretch ratio on this occasion is from 0.2 to 4%, is performed between a takeoff roller and a first stretch roller, a first stretch satisfying such conditions as the fiber temperature of from 130° C. to 180° C. and stretch tensile force of not more than the prestretch tensile force is performed between the first stretch roller and a second stretch roller at the first stretch, the total stretch magnification including subsequent stretches is set to 5 or more, and finally heat-treatment under tension with a stretch ratio of from 0 to 2% is performed.
5. The method for producing a polyethylene naphthalate fiber according to claim 4 , wherein the stretch tensile force at the first stretch is in the range of from 15 to 80% of the prestretch tensile force.
6. The method for producing a polyethylene naphthalate fiber according to claim 4 , wherein the stretch tensile force at the first stretch is from 0.1 to 0.6 cN/dtex.
7. The method for producing a polyethylene naphthalate fiber according to claim 4 , wherein the stretch speed is from 2000 to 4000 m/min.
8. The method for producing a polyethylene naphthalate fiber according to claim 4 provided with a heating zone immediately beneath the spinneret, the zone having a length of 300 mm or less.
9. The method for producing a polyethylene naphthalate fiber according to claim 6 , wherein the fiber spinning speed is from 400 to 800 m/min.
10. The method for producing a polyethylene naphthalate fiber according to claim 4 , wherein the birefringence index Δn of the fiber before the stretch is from 0.001 to 0.01.
11. A polyethylene naphthalate fiber cord for industrial material, the fiber cord being a multifilament composed of the polyethylene naphthalate fiber as described in claim 1 .
12. The polyethylene naphthalate fiber cord for industrial material according to claim 11 , wherein an adhesive treatment agent is given onto the surface of the multifilament.
13. The polyethylene naphthalate fiber cord for industrial material according to claim 12 , wherein the adhesive treatment agent is a resorcin-formalin latex adhesive agent.
14. The polyethylene naphthalate fiber cord for industrial material according to claim 11 , wherein the number of twists of the multifilament is from 50 to 1000 turn/m.
15. The polyethylene naphthalate fiber according to claim 1 wherein a Silk factor, which is defined by (strength (cN/dtex))×(square root of elongation degree (%)), is in the range of from 22 to 30.