Polyurethane foam
Polymer-modified polyol, for use as a starting material for polyurethane foam, is made by reacting an olamine, such as triethanolamine, with an isocyanate in the presence of a metal organic catalyst. The catalyst is a metal salt of an organic acid and the viscosity of the polymer-modified polyol is at least 2250 mPa·s. In one embodiment the catalyst is of the formulat M(O.CO.R.CH 3 ) 2 where M is a metal and R is a carbon chain of 6 to 20 carbons. A metal salt of a monohydroxy fatty acid, particularly ricinoleic acid may be used.
1. A method of making a polymer-modified polyol, wherein an olamine is reacted with an organic polyisocyanate in the presence of a polyol and at least one catalyst which is a metal salt of an organic acid, the olamine reacting at least predominantly polyfunctionally with the isocyanate, wherein the, or at least one, catalyst is present in a proportion of 0.006-0.01 mmol/100 grams polyol, and wherein the viscosity of the polymer-modified polyol is at least 2250 mPa·s. when measured at 25° C. using a Brookfield or Brookfield compatible viscometer.
2. The method according to claim 1 , wherein the viscosity of the polymer-modified polyol is at least 2400 mPa·s.
3. The method according to claim 1 , wherein the viscosity of the polymer-modified polyol is at least 2500 mPa·s.
4. The method according to claim 1 , wherein the at least one catalyst is of the formula:
M(O.CO.R.CH 3 ) 2
where M is a metal
R is a carbon chain of 6 to 20 carbons.
5. A method of making a polymer-modified polyol, wherein an olamine is reacted with an organic polyisocyanate in the presence of a polyol and at least one catalyst which is present in a proportion of 0.006-0.012 mmol/100 grams polyol and is a metal salt of an organic acid, the olamine reacting at least predominantly polyfunctionally with the isocyanate, wherein the, or at least one, said catalyst is of the formula:
M(O.CO.R.CH 3 ) 2
where M is a metal
R is a carbon chain of 6 to 20 carbons.
6. The method according to claim 5 , wherein R is a carbon chain of 6 to 16 carbons.
7. The method according to claim 6 , wherein the at least one catalyst is a metal salt of a monohydroxy fatty acid.
8. A method of making a polymer-modified polyol, wherein an olamine is reacted with an organic polyisocyanate in the presence of a polyol and at least one catalyst which is present in a proportion of 0.006-0.012 mmol/100 grams polyol and is a metal salt of an organic acid, the olamine reacting at least predominantly polyfunctionally with the isocyanate, wherein the, or at least one, said catalyst is a metal salt of a monohydroxy fatty acid.
9. The method according to claim 8 , wherein the at least one catalyst is a metal ricinoleate salt.
10. The method according to claim 9 , wherein the at least one catalyst is selected from the group consisting of tin and zinc diricinoleate.
11. The method according to claim 1 , wherein the at least one catalyst is selected from the group consisting of Stannous octoate, Stannous dilaurate, Stannous dipalmitate, Stannous distearate, Stannous dioleate, Zinc octoate, and Zinc dineodecanoate.
12. The method according to claim 1 , wherein the at least one catalyst is selected from the group consisting of Bismuth trineodecanoate, Potassium octoate, and Zirconium octoate.
13. The method according to claim 1 , wherein the olamine is triethanolamine.
14. The method according to claim 13 , wherein the polyol is at least predominantly a polyether polyol.
15. The method according to claim 14 , wherein the isocyanate is selected from the group consisting of TDI (toluene diisocyanate) and MDI (methylene diphenyl isocyanate).
16. The method according to claim 15 , wherein the isocyanate index is 90-120.
17. The method according to claim 16 , wherein the isocyanate index is 95 to 111.
18. A polymer-modified polyol made by the method of claim 17 .
19. A method of making polyurethane foam, wherein the polymer-modified polyol of claim 18 is reacted with an isocyanate in the presence of a metal carboxylate catalyst to form polyurethane material which is foamed.
20. The method according to claim 19 , wherein the metal carboxylate catalyst is a metal salt of an organic acid having no metal-carbon bond.
21. The method according to claim 20 , wherein the metal carboxylate catalyst is a metal salt of a monohydroxy fatty acid.
22. The method according to claim 20 wherein the metal carboxylate catalyst is selected from the group consisting of tin octoate and tin diricinoleate.
23. The method according to claim 19 , wherein the metal carboxylate catalyst is the same as the metal carboxylate catalyst used in forming the polymer-modified polyol.
24. Flexible polyurethane foam made by the method of claim 19 .
25. Polyurethane foam according to claim 24 which is a high resilience foam.