Packing material for battery case and battery case
A battery case material includes a biaxially stretched polyamide film layer as an outer layer, a thermoplastic resin unstretched film layer as an inner layer, and an aluminum foil layer interposed between the two film layers. As the biaxially stretched polyamide film, a biaxially stretched polyamide film having a density of 1,130 to 1,160 kg/m 3 is used. In the battery case material, excellent formability can be secured without coating a lubrication giving component, and sufficient volume capacity ratio can be obtained.
1. A battery case material comprising:
an outer layer comprising a biaxially stretched polyamide film;
an inner layer comprising a thermoplastic resin unstretched film; and
an aluminum foil layer interposed between the outer and inner layers,
wherein the biaxially stretched polyamide film is obtained by a simultaneous biaxial stretching method and setting a heat setting temperature in a range of 200° C. to 205° C. during stretching of the simultaneous biaxial stretching method, and the biaxially stretched polyamide film has a density of 1,142 to 1,146 kg/m 3 .
2. The battery case material as recited in claim 1 , wherein the biaxially stretched polyamide film is a biaxially stretched nylon film and is 15 to 20 μm in thickness.
3. The battery case material as recited in claim 1 , wherein the biaxially stretched polyamide film is 12 to 50 μm in thickness, the thermoplastic resin unstretched film is 20 to 80 μm in thickness, and the aluminum foil layer is 5 to 50 μm in thickness.
4. The battery case material as recited in claim 1 , further comprising a urethane series adhesive layer, wherein the biaxially stretched polyamide film and the aluminum foil layer are integrally laminated via the urethane series adhesive layer.
5. A battery case comprising a battery case material according to claim 1 , wherein the battery material is formed by deep drawing.
6. A battery case comprising a battery case material according to claim 1 , wherein the battery material is formed by stretch forming.
7. The battery case material as recited in claim 1 , wherein the biaxially stretched polyamide film is a biaxially stretched nylon film.
8. The battery case material as recited in claim 1 , wherein the biaxially stretched polyamide film is 12 to 50 μm in thickness.
9. The battery case material as recited in claim 1 , wherein the biaxially stretched polyamide film is 12 to 50 μm in thickness, and the biaxially stretched polyamide film is a biaxially stretched nylon film.
10. The battery case material as recited in claim 1 , wherein the biaxially stretched polyamide film is 15 to 20 μm in thickness.
11. The battery case material as recited in claim 3 , wherein the biaxially stretched polyamide film is 15 to 20 μm in thickness, and the biaxially stretched polyamide film is a biaxially stretched nylon film.