Bakeable, screen-printable anti-reflection coating for glass
A composition for the production of an antireflection coating, comprising a condensate obtainable by the condensation of silicon compounds of the general formula R n SiX 4-n (I) in which the X groups are the same or different and represent hydrolyzable groups or hydroxyl groups, the R groups are the same or different and represent non-hydrolyzable groups, and n is 0, 1, 2, or 3, wherein the composition comprises at least one polymeric agent controlling the rheology and at least one solvent with a boiling point of at least 150° C. The present invention also describes methods for the preparation and use of the present composition. In particular, the composition can be applied by screen printing methods on substrates.
1. A colloidal solution composition for the production of an anti-reflection coating, comprising
(a) colloidal particles of an SiO 2 condensate obtained by condensation, in the presence of at least one hydroxyl-containing polymeric flow control agent, of silicon compounds of the general formula
R n SiX 4-n (I),
in which the residues X are the same or different and signify hydrolysable groups or hydroxyl groups, the residues R are the same or different and signify non-hydrolysable groups and n is 0, 1, 2 or 3,
(b) 5 to 15 wt % of at least one polymeric flow control agent and
(c) at least one solvent having a boiling point of at least 150° C.
2. The composition according to claim 1 , characterised in that the composition has a viscosity in the range of from 1.0 to 6 Pa*s at a shear of 0.5 s −1 and a temperature of 25° C.
3. The composition of claim 1 , wherein the composition has a viscosity in the range of from 0.8 Pa*s to 2.5 Pa*s at a shear of 30 s −1 and a temperature of 25° C.
4. The composition of claim 1 , characterised in that the flow control agent is at least one of cellulose ether and cellulose ester.
5. The composition of claim 1 , wherein the flow control agent has a molecular weight M w in the range of from 500 to 500000 g/mol.
6. The composition of claim 1 , wherein the condensate is obtained by condensation of a mixture comprising at least one silicon compound of the formula SiX 4 , in which the residues X are the same or different and signify hydrolysable groups or hydroxyl groups.
7. The composition according to claim 6 , characterised in that the proportion of the silicon compound according to the formula SiX 4 is in the range of from 20 wt. % to 80 wt. %, based on the total quantity of monomeric silicon compounds.
8. The composition of claim 6 , wherein the composition contains at least 60 wt. % solvent having a boiling point of at least 150° C.
9. The composition of claim 1 , wherein the condensate is obtained by condensation of a mixture comprising at least one silicon compound of the formula RSiX 3 , in which the residues X are the same or different and signify hydrolysable groups or hydroxyl groups and the residue R signifies a non-hydrolysable groups.
10. The composition of claim 1 , wherein the condensate is obtained by condensation of a mixture comprising at least one silicon compound of the formula R 2 SiX 2 , in which the residues X are the same or different and signify hydrolysable groups or hydroxyl groups and the residues R are the same or different and signify non-hydrolysable groups.
11. The composition of claim 1 , wherein the condensate is obtained by condensation of a mixture comprising at least one silicon compound of the formula R 3 SiX, in which the residue X signifies a hydrolysable group or a hydroxyl group and the residues R are the same or different and signify non-hydrolysable groups.
12. The composition according to claim 1 , wherein the composition has at least 70 wt. % solvent.
13. The composition of claim 1 , wherein the solvent has a boiling point of at least 200° C.
14. The composition of claim 1 , wherein the condensate was produced in the presence of at least one polymeric flow control agent and at least one solvent having a boiling point of at least 150° C.
15. The composition of claim 1 , wherein the proportion of SiO 2 condensate in the composition is in the range of from 0.01 wt. % to 5 wt. %.
16. A process for the production of an anti-reflection coating, wherein the composition of claim 1 is applied to a substrate and baked to obtain a nanoporous layer.
17. The process according to claim 16 , characterised in that the composition is applied by screen-printing methods or roller-coating methods.
18. The process of claim 16 , wherein the composition is baked at a temperature in the range of from 550° C. to 750° C.
19. The process of claim 16 , wherein the film thickness of the anti-reflection coating is adjusted by mixing the composition with a mixture containing solvents and flow control agents.
20. The process of claim 16 , wherein the baking takes place in a sheet glass furnace or hardening furnace.
21. A process for producing the colloidal solution composition of claim 1 , comprising (1) mixing (a) at least one solvent having a boiling point of at least 150° C., (b) 5 wt % to 15 wt % of at least one flow control agent, (c) water and (d) at least one compound of the general formula
R n SiX 4-n (I),
in which the residues are the same or different and R signifies an organic residue with 1 to 10 carbon atoms, which are optionally interrupted by at least one of oxygen atoms, sulfur atoms and amino groups, X denotes hydrogen, halogen, hydroxy, alkoxy, acyloxy, alkylcarbonyl, alkoxycarbonyl or NR′ 2 , with R′ equal to hydrogen, alkyl or aryl and n equal to 0, 1, 2 or 3, and (2) condensing the compounds of formula (I).
22. The process according to claim 21 , characterised in that the condensation is catalysed with an acidic or a basic compound.
23. The process according to claim 21 , characterised in that the condensation is catalysed with at least one of ammonia and an ammonium salt.
24. The process of claim 21 , wherein the quantity of water added is selected such that no more than 20 wt. % of the water is separated off by distillation during or after the condensation.
25. The process of claim 21 , wherein the composition is produced in a single process step, wherein the individual components are mixed and condensed.