Golf ball
A golf ball component, such as a golf ball cover layer, formed from a high or increased melt index thermoplastic polyurethane, polyurea or polyurethane/polyurea is disclosed. The cover layer may be relatively thin (i.e., 0.075 or less, preferably 0.050 inches or less, more preferably less than 0.040 inches, even more preferably less than 0.030 inches). In addition, an operation in which the outer cover is exposed to an isocyanate solution is described to improve certain physical properties of the resulting golf ball.
1. A method of producing a golf ball, the method comprising:
forming a molded core from a core material, the core having a mass ranging from 25 grams to 40 grams;
molding a cover layer from a cover material having a melt index of 15 g/10 minutes or more at a temperature of 200° C. to 210° C. and a load of 8.7 Kg, the cover material comprising a polyurethane, polyurea or blends thereof;
applying an isocyanate to the cover layer for a time period of from about 1 minute to about 10 minutes.
2. The method according to claim 1 wherein the isocyanate is selected from the group consisting of 4,4′-diphenylmethane diisocyanate (“MDI”); 2,4-toluene diisocyanate (“TDI”); m-xylylene diisocyanate (“XDI”); methylene bis-(4-cyclohexyl isocyanate) (“HMDI”); hexamethylene diisocyanate (“HDI”); naphthalene-1,5,-diisocyanate (“NDI”); 3,3′-dimethyl-4,4′-biphenyl diisocyanate (“TODI”); 1,4-diisocyanate benzene (“PPDI”); phenylene-1,4-diisocyanate; 2,2,4- or 2,4,4-trimethyl hexamethylene diisocyanate (“TMDI”); isophorone diisocyanate (“IPDI”); 1,4-cyclohexyl diisocyanate (“CHDI”); diphenylether-4,4′-diisocyanate; p,p′-diphenyl diisocyanate; lysine diisocyanate (“LDI”); 1,3-bis(isocyanato methyl)cyclohexane; polymethylene polyphenyl isocyanate (“PMDI”); meta-tetramethylxylylene diisocyanate (“TMXDI”); and combinations thereof.
3. The method according to claim 1 wherein the isocyanate is MDI.
4. The method according to claim 1 wherein the isocyanate is applied to the cover layer by an operation selected from the group consisting of dipping, wiping, soaking, spraying, brushing, and combinations thereof.
5. The method according to claim 1 wherein the cover material has a melt index of 20 g/10 min or ore at a temperature of 200° C. to 210° C. and a load of 8.7 kg prior to molding.
6. The method according to claim 1 wherein the cover material has a melt index of 25 g/10 min or ore at a temperature of 200° C. to 210° C. and a load of 8.7 kg prior to molding.
7. The method according to claim 1 wherein the cover material has a melt index of 30 g/10 min or ore at a temperature of 200° C. to 210° C. and a load of 8.7 kg prior to molding.
8. A method for producing a golf ball, the method comprising:
forming a molded core from a core material, the core having a mass ranging from 25 grams to 40 grams;
molding a cover layer from a cover material comprising a polyurethane, the cover material exhibiting a melt index of from about 35 to about 85 grams per 10 minutes at a temperature of 200° C. to 210° C. and a load of 8.7 kg; and
applying 4,4′-diphenylmethane diisocyanate to the molded cover layer.
9. The method according to claim 8 further comprising forming one or more intermediate layers between the core and the cover layer.