Flame-proofed thermoplastic compositions
Flame-proofed thermoplastic compositions include organophosphorus compounds as flame retardants; thermoplastic articles shaped therefrom do not experience deterioration of the appearance of the surfaces thereof by corrosion or deposition.
1. A method of reducing at least one of corrosion of a metal part and deposition of a flame retardant on a surface of a metal part, said method comprising:
shaping a thermoplastic matrix comprising at least one phosphinic acid salt of formula (I):
in which:
R 1 and R 2 , which may be identical or different, are each a linear or branched alkyl radical having from 1 to 6 carbon atoms, and/or an aryl radical;
M is a calcium, magnesium, aluminum and/or zinc ion; and
Z is 2 or 3, by a plastic conversion or forming technique selected from the group consisting of extrusion, molding and injection, thereby obtaining a thermoplastic shaped part in a solid state; and
placing said thermoplastic part in a solid state in contact with, or within approximately 1 cm of said metal part in a solid state.
2. The process as defined by claim 1 , wherein the thermoplastic shaped part comprises from 1 to 30% by weight of organophosphorus compounds.
3. The process as defined by claim 1 , wherein the thermoplastic shaped part also comprises a compound that is the reaction product from phosphoric acid and melamine and/or the reaction product from phosphoric acid and a melamine condensation derivative.
4. The process as defined by claim 1 , wherein the thermoplastic shaped part is produced from a thermoplastic matrix recited from the group consisting of olefin resins, polyethylene, polypropylene and polybutylene, polyisobutylene, styrene resins, polystyrenes and acrylonitrile-butadiene-styrene copolymers, polyamides, polyacetals, polyesters, polyethylene terephthalate and polybutylene terephthalate, polycarbonates, polyester carbonates, polysulfone resins, polyphenylene oxides, polyphenylene ethers, polyphenyiene sulfides, vinyl polymers and copolymers thereof, polyvinyl acetate, polyvinyl alcohol, polyvinyl chloride, derivatives thereof and/or mixtures thereof.
5. The process as defined by claim 1 , wherein the thermoplastic shaped part comprises a polyamide matrix selected from the group consisting of polyimide PA 6, polyarnide PA 6,6, polyimide PA-11, polyimide PA 12, polymetaxylylenediamine, and blends and copolymers thereof.