Dry mix for treating refractory substrates and process using same
Dry mix for treating refractory substrates, comprising combustible particles of at least one oxidizable substance which, in the presence of oxygen, gives rise to an exothermic reaction, and particles of at least one other substance, wherein these particles form together, during said exothermic reaction, a coherent mass capable of adhering to and/or interacting with the treated substrate, characterized in that it comprises, as particles of at least one other substance, particles of at least one expanding substance, in that the dry mix without the particles of this at least one expanding substance has a first bulk density and in that the mix comprising said at least one expanding substance has a second bulk density lower than said first bulk density.
1. Dry mix for treating refractory substrates, comprising
combustible particles of at least one oxidizable substance which, in the presence of oxygen, gives rise to an exothermic reaction, and
particles of at least one other substance,
wherein these particles together form, during said exothermic reaction, a coherent mass capable of adhering to and/or interacting with a treated substrate,
this mix comprising, as particles of at least one other substance, particles of at least one expanding substance, the dry mix without the particles of this at least one expanding substance having a first bulk density and the dry mix comprising said at least one expanding substance having a second bulk density lower than said first bulk density,
characterised in that said mix also comprises, as particles of at least one other substance, particles of at least one siliceous glass, which have a weight fraction greater than any other constituent in the mix, said mix containing:
a) 45 to 60% by weight of siliceous glass particles;
b) 20 to 30% by weight of combustible particles;
c) 5 to 10% by weight of expanded perlite particles; and
d) 10 to 25% by weight of silica particles.
2. Mix according to claim 1 , characterised in that the expanded perlite consists of grains of a density of less than 2.
3. Mix according to claim 1 , characterised in that the silica particles are selected from the group consisting of vitreous or fused silica, crystalline silica and mixtures thereof.
4. Mix according to claim 1 , characterised in that the siliceous glass particles are selected from the group consisting of silico-sodo-calcic glasses, borosilicates, cullet or broken glass, and mixtures thereof.
5. Mix according to claim 1 , characterised in that it has a weight ratio between the particles of siliceous glass and the particles of silica of between 3/1 and 6/1.
6. Mix according to claim 1 , characterised in that said combustible particle is selected from the group consisting of Si, Al, Zr, Mg, Ca, Fe, Cr, Ti, and combinations and alloys thereof.
7. Mix according to claim 1 , characterised in that the maximum size of the particles of expanded perlite is less than or equal to 1 mm.
8. Mix according to claim 1 , characterised in that the maximum size of the combustible particles is less than or equal to 100 μm.
9. Mix according to claim 1 , characterised in that the maximum size of the silica particles is less than or equal to 0.5 mm.
10. Mix according to claim 1 , characterised in that the maximum size of the siliceous glass particles is less than or equal to 1 mm.