Method for the preparation of fluoropolymer powdered materials
A method for the preparation of a modified fluoropolymer powdered material is disclosed. A suspension of solid fluoropolymer particles together with PTFE particles in an aqueous carrier, is frozen and the frozen carrier is then removed by sublimation at sub-atmospheric pressure to produce a dry powder of modified fluoropolymer particles.
1. A method for the preparation of a modified fluoropolymer material in powder form which comprises the steps of:
forming a suspension of solid particles of the fluoropolymer together with particles of polytetrafluoroethylene (PTFE) as a modifier in an aqueous liquid carrier;
freezing the aqueous suspension; and
subsequently subjecting the frozen aqueous suspension to sublimation, thereby producing dry particles of the fluoropolymer, modified by the presence of the PTFE modifier, in powder form.
2. The method of claim 1 , wherein the fluoropolymer comprises perfluoromethyl vinyl ether (MFA).
3. The method of claim 1 , wherein the particle size of the fluoropolymer is in the range 30 to 350 nm.
4. The method of claim 1 , wherein the PTFE modifier has a particle size in the range 30 to 350 nm.
5. The method of claim 1 , wherein the PTFE is present as up to 50 wt % of the MFA/PTFE mixture, expressed on a dry weight basis.
6. The method of claim 1 , wherein sublimation is achieved by means of a sub-atmospheric pressure.
7. The method of claim 6 , wherein the reduced pressure is in the range of 0.01 to 0.99 atm.
8. The method of claim 1 , wherein sublimation is carried out at a temperature below the glass transition temperature of the fluoropolymer.
9. The method of claim 8 , wherein sublimation is carried out at ambient temperature.
10. The method of claim 8 , wherein sublimation is carried out at a temperature between ambient temperature and the glass transition temperature of the fluoropolymer.
11. The method of claim 1 , wherein the suspension of the solid particles in the aqueous carrier is frozen at a temperature in the range −60° C. to −20° C.
12. The method of claim 1 , wherein the suspension of the solid particles in the aqueous carrier is frozen in trays.
13. The method of claim 1 , wherein the modified fluoropolymer particles are subjected to milling.
14. The method of claim 1 , wherein the modified fluoropolymer particles are subjected to irradiation.
15. The method of claim 1 , wherein the fluoropolymer is fibrillatable.
16. The method of claim 1 , wherein the fluoropolymer is non-pumpable.
17. The method of claim 1 , wherein the fluoropolymer is perfluoro alkoxy (PFA).
18. The method of claim 1 , wherein the fluoropolymer is fluoro ethylene propylene (FEP).
19. The method of claim 1 , further comprising the additional step of spraying the powder onto a substrate.