Filled polymeric membranes, use and method of manufacturing
View Patent ↗A method of manufacturing a filled polymeric membrane includes a first step of preparing a filler suspension having a solvent for a glassy polymer and nanometer-sized particles. The nanometer-sized particles in the filler suspension are aggregated in aggregates having an average aggregate size in the range between 50 nm and smaller than 200 nm. In a following step, the glassy polymer is added to the filler suspension to obtain a polymer suspension. Next, the glassy polymer is dissolved in the polymer suspension. In a next step, the polymer suspension is cast on a substrate, followed by a step of removing the solvent. A filled polymeric membrane includes aggregates of nanometer-sized filler particles. The membrane is used in pervaporation and nanofiltration.
1. A filled polymeric membrane for separating a mixture of fluids, the membrane comprising:
a glassy polymer having a glass transition temperature of at least 100° C.; and
nanometer-sized filler particles, wherein said filler particles are arranged in aggregates, the aggregates having an average aggregate size of at least 50 nm and smaller than 200 nm, wherein the size distribution of said aggregates has a standard deviation smaller than or equal to 150 nm.
2. The filled polymeric membrane according to claim 1 , comprising a porous support.
3. The filled polymeric membrane according to claim 1 , wherein the nanometer-sized particles have a size between 1 nm and 25 nm.
4. The filled polymeric membrane according to claim 1 , wherein the nanometer-sized particles comprise hyrdrophobic silica.
5. The filled polymeric membrane according to claim 1 , wherein the glassy polymer is a substituted polyacetylene polymer or an amorphous perfluouropolymer.
6. The filled polymeric membrane according to claim 5 , wherein the glassy polymer is a copolymer of tetrafluoroethylene and 2,2-bis(trifluoromethyl)-4,5-difluoro-1,3-dioxle, or a copolymer of tetrafluoroethylene and 2,2,4-trifluoro-5-trifluoromethoxy-1,3 dioxole.
7. The filled polymeric membrane according to claim 1 , wherein the glassy polymer is poly(1-trimethylsilyl-1-propyne) or poly(4-methyl-2-pentyne).
8. The filled polymeric membrane according to claim 1 , wherein nanometer-sized particles form between 0.01% and 90% by weight of the membrane.
9. A filled polymeric membrane for separating a mixture of fluids, the membrane comprising:
a glassy polymer having a glass transition temperature of at least 100° C.; and nanometer-sized filler particles, wherein said filler particles are arranged in aggregates, the aggregates having an average aggregate size of at least 50 nm and smaller than 200 nm, wherein between 51% and 90% of the aggregates have a size smaller than 200nm.
10. The filled polymeric membrane according to claim 9 , comprising a porous support.
11. The filled polymeric membrane according to claim 9 , wherein the nanometer-sized particles comprise hyrdrophobic silica.
12. The filled polymeric membrane according to claim 9 , wherein the glassy polymer is a substituted polyacetylene polymer or an amorphous perfluouropolymer.
13. The filled polymeric membrane according to claim 12 , wherein the glassy polymer is a copolymer of tetrafluoroethylene and 2,2-bis(trifluoromethyl)-4,5-difluoro-1 ,3-dioxle, or a copolymer of tetrafluoroethylene and 2,2,4-trifluoro-5-trifluoromethoxy-1,3 dioxole.
14. The filled polymeric membrane according to claim 9 , wherein the glassy polymer is poly(1-trimethylsilyl-1-propyne) or poly(4-methyl-2-pentyne).
15. A filled polymeric membrane for separating a mixture of fluids, the membrane comprising:
a glassy polymer having a glass transition temperature of at least 100° C.; and nanometer-sized filler particles, wherein said filler particles are arranged in aggregates, the aggregates having an average aggregate size of at least 50 nm and smaller than 200 nm, wherein between 10% and 40% of the aggregates have a size smaller than 100 nm, between 20% and 75% of the aggregates have a size between 100 nm and 200 nm and between 0% and 49% of the aggregates have a size larger than 200nm.
16. The filled polymeric membrane according to claim 15 , comprising a porous support.
17. The filled polymeric membrane according to claim 15 , wherein the nanometer-sized particles comprise hyrdrophobic silica.
18. The filled polymeric membrane according to claim 15 , wherein the glassy polymer is a substituted polyacetylene polymer or an amorphous perfluouropolymer.
19. The filled polymeric membrane according to claim 18 , wherein the glassy polymer is a copolymer of tetrafluoroethylene and 2,2-bis(trifluoromethyl)-4,5-difluoro-1,3-dioxle, or a copolymer of tetrafluoroethylene and 2,2,4-trifluoro-5-trifluoromethoxy-1,3 dioxole.
20. The filled polymeric membrane according to claim 15 , wherein the glassy polymer is poly(1-trimethylsilyl-1-propyne) or poly(4-methyl-2-pentyne).