Surface enhanced infrared absorption sensor and method for producing the same
The method for producing a surface enhanced infrared absorption sensor of the invention is characterized by: adsorbing metallic nanoparticles dispersed in a solution on a surface of a substrate, or allowing the adsorbed metallic nanoparticles to be grown in a solution, thereby forming a film; applying infrared light to the substrate from the side thereof opposite to the side on which the metallic nano-thin film is disposed; detecting evanescent waves exuding from the substrate; and regulating a surface enhanced infrared adsorption activity while monitoring surface enhanced infrared adsorption signals in situ, whereby the metallic nano-thin film is grown in the form of flat and discontinuous islands. According to the method, there is provided a production technique for a surface enhanced infrared absorption (SEIRA) sensor having a higher sensitivity and more excellent in the reproducibility.
1. A surface enhanced infrared absorption sensor material with a metallic nano-thin film adsorbed on a dielectric substrate, wherein the metallic nano-thin film is disposed on the substrate as flat and discontinuous islands having a two-dimensional filling factor from 0.7 to less than 1, the average gap between the adjacent islands is from 3 nm to 7 nm, and the degree of flatness, that is, the average value of the proportion of the thickness to the width of the island-like metallic nano-thin film is at most 0.2.
2. A method for producing a surface enhanced infrared absorption sensor with a metallic nano-thin film adsorbed on a dielectric substrate, characterized by:
adsorbing metallic nanoparticles dispersed in a solution on a surface of a substrate;
growing a film by using the adsorbed metallic nanoparticles as growing nuclei at the liquid solid interface in a solution;
applying infrared light to the substrate from the side thereof opposite to the side on which the metallic nano-thin film is disposed;
monitoring the reflected beam from the metal-substrate interface; and
forming the metallic nano-thin film in the form of flat and disconnected islands by stopping the growth of the metallic nano-thin film at the growth stage when the surface enhanced infrared adsorption activity becomes maximum while monitoring surface enhanced infrared adsorption signals in situ, said metallic nano-thin film disposed on the substrate as flat and disconnected islands having a two-dimensional filling factor from 0.7 to less than 1, the average gap between the adjacent islands being from 3 nm to 7 nm, and the degree of flatness, that is, the proportion of the thickness to the width of the island-like metallic nano-thin film being at most 0.2.
3. The method for producing a surface enhanced infrared absorption sensor as claimed in claim 2 , wherein the irradiation with infrared light is monitored according to an attenuated total reflectance method.