Process for the preparation of polyether polyols
The present invention provides a process for conditioning double metal cyanide (DMC) catalysts, which are employed in the preparation of polyether polyols based on starter compounds having active hydrogen atoms, the preparation of polyether polyols using the conditioned catalysts and the use of the polyether polyols prepared in this way for the preparation of polyurethane materials.
1. A process for the preparation of polyether polyols with continuous metering and reacting of starter compounds and alkylene oxides, including a conditioned double metal cyanide (DMC) catalyst, said double metal cyanide catalyst being conditioned by dispersing said double metal cyanide catalyst in starting media having an OH number of from about 5 to 500 mg KOH/g, in which the starting media is selected from the group consisting of addition products of starter compounds having Zerewitinoff-active hydrogen atoms and alkylene oxides, poly(ester) polyols, polycarbonate polyols, hydroxylated triglycerides, hydroxylated fatty acid derivatives and mixtures thereof, at a temperature of from about 0° C. to about 80° C. over a period of from about 5 minutes to about 4 hours under pressure of from about 1 mbar to about 10 bar.
2. A continuous process for the preparation of polyether polyols with continuous metering and reacting of starter compounds, alkylene oxides and a conditioned double metal cyanide catalyst, said double metal cyanide catalyst being conditioned by dispersing said double metal cyanide catalyst in starting media having an OH number of from about 5 to 500 mg KOH/g, in which the starting media is selected from the group consisting of addition products of starter compounds having Zerewitinoff-active hydrogen atoms and alkylene oxides, poly(ester) polyols, polycarbonate polyols, hydroxylated triglycerides, hydroxylated fatty acid derivatives and mixtures thereof, at a temperature of from about 0° C. to about 80° C. over a period of from about 5 minutes to about 4 hours under an inert gas atmosphere.
3. A process for the preparation of a polyether polyol, comprising alkoxylating a starter compound in the presence of a conditioned double metal cyanide catalyst, said double metal cyanide catalyst being conditioned by dispersing said double metal cyanide catalyst in starting media having an OH number of from about 5 to 500 ma KOH/g, in which the starting media is selected from the group consisting of addition products of starter compounds having Zerewitinoff-active hydrogen atoms and alkylene oxides, poly(ester) polyols, polycarbonate polyols, hydroxylated triglycerides, hydroxylated fatty acid derivatives and mixtures thereof, at a temperature of from about 0° C. to about 80° C. over a period of from about 5 minutes to about 4 hours under pressure of from about 1 mbar to about 10 bar; wherein the total amount of starter compound employed for the preparation of the polyether polyols is already present in the starting medium during the conditioning of the DMC catalyst.
4. The process of claim 1 , further comprising the step of reacting the polyether polyol with an isocyanate component to make a polyurethane material.
5. The process of claim 2 , further comprising the step of reacting the polyether polyol with an isocyanate component to make a polyurethane material.
6. The process of claim 3 , further comprising the step of reacting the polyether polyol with an isocyanate component to make a polyurethane material.