Chitosan-based adhesives and uses thereof
There is provided an adhesive comprising chitosan an optionally a crosslinking agent. A method for preparing such an adhesive is also disclosed. A wood-panel made with such an adhesive is also provided. Moreover, a method for manufacturing a wood-based panel is provided. The method comprises preparing a mixture comprising wood, chitosan, optionally a crosslinking agent, and optionally an acid, forming a mat with the mixture, and pressing the mat under heat and pressure so as to obtain the wood-based panel.
1. An adhesive comprising hydrolyzed chitosan obtained by a chemical process consisting of an acid hydrolysis of chitosan or obtained by enzymatic hydrolysis of chitosan, an acid and a crosslinking agent that is phenylglyoxal, wherein said adhesive has a curing time of about 30 seconds to about 120 seconds at a temperature comprised between 60° C. and 120° C.
2. The adhesive of claim 1 , wherein said crosslinking agent is present in said adhesive at a molecular ratio crosslinking agent:hydrolyzed chitosan of about 1:40 to about 1:10.
3. The adhesive of claim 1 , wherein said crosslinking agent is present in said adhesive at a molecular ratio crosslinking agent:hydrolyzed chitosan of about 1:30 to about 1:15.
4. The adhesive of claim 1 , wherein said adhesive further comprises water.
5. The adhesive of claim 1 , wherein said acid is chosen from formic acid, acetic acid, propionic acid, glycolic acid, and mixtures thereof.
6. The adhesive of claim 1 , wherein said acid is acetic acid.
7. The adhesive of claim 6 , wherein said adhesive has a molecular ratio acid:hydrolyzed chitosan of about 1:1 to about 1:4.
8. The adhesive of claim 6 , wherein said hydrolyzed chitosan and said crosslinking agent are in admixture with said acetic acid, and said chitosan has a concentration of about 15 to about 25% m/v.
9. The adhesive of claim 6 , wherein said hydrolyzed chitosan is in a dry powder form before being in admixture with said acetic acid and said crosslinking agent.
10. A wood-based panel obtained by pressing, during a pressing time of about 20 seconds to about 225 seconds, a wood-based mat comprising an adhesive comprising hydrolyzed chitosan, an acid and a crosslinking agent that is phenylglyoxal, wherein said adhesive has a curing time of about 30 seconds to about 120 seconds at a temperature comprised between 60° C. and 120° C. and wherein said wood-based panel is chosen from an oriented strandboard, a low density fiberboard, a medium density fiberboard, a high density fiberboard, a particle board, and a hardboard.
11. The wood-based panel of claim 10 , wherein said acid is chosen from formic acid, acetic acid, propionic acid, glycolic acid, and mixtures thereof.
12. The wood-based panel of claim 10 , wherein said acid is acetic acid.
13. The wood-based panel of claim 10 , wherein said wood-based panel has an internal bond of at least about 1.0 N/mm 2 .
14. A wood-based panel comprising wood and an adhesive comprising hydrolyzed chitosan obtained by a chemical process consisting of an acid hydrolysis of chitosan or obtained by enzymatic hydrolysis of chitosan, an acid and a crosslinking agent that is phenylglyoxal, and wherein said adhesive is at least partially cured, said wood-based panel being chosen from an oriented strandboard, a low density fiberboard, a medium density fiberboard, a high density fiberboard, a particle board, and a hardboard, and wherein said crosslinking agent is present in said adhesive at a molecular ratio crosslinking agent:hydrolyzed chitosan of about 1:40 to about 1:10 and said adhesive has a molecular ratio acid:hydrolyzed chitosan of about 1:1 to about 1:4.
15. The wood-based panel of claim 14 , wherein said wood-based panel has an internal bond of at least about 1.0 N/mm 2 .
16. The wood-based panel of claim 14 , wherein said acid is chosen from formic acid, acetic acid, propionic acid, glycolic acid, and mixtures thereof.
17. The wood-based panel of claim 14 , wherein said acid is acetic acid.