HARD COAT FILM
A high-hardness hard coat film having a reduced degree of curling and an ionizing ray polymerizable resin composition for forming the hard coat layer of such a hard coat film are provided. The hard coat film includes a resin film and a hard coat layer disposed on the surface of the resin film. The hard coat layer is formed of a cured product of a photopolymerizable composition containing an acrylic component, a hyperbranched acrylate resin, a silicone component, and silica particles. The cured product is produced by exposure to ionizing rays.
1 . An ionizing ray polymerizable resin composition for forming a hard coat layer, the composition comprising:
65.0 parts by weight or more and 95 parts by weight or less of an acrylic component including one or both of a polyfunctional acrylic monomer and a polyfunctional acrylic oligomer having a linear main skeleton or a main skeleton having one branch point;
0.5 parts by weight or more and 12 parts by weight or less of a silicone component including one or both of a silicone monomer having an acryloyl group at a terminal thereof and a silicone oligomer having an acryloyl group at a terminal thereof;
2.0 parts by weight or more and 20.0 parts by weight or less of a hyperbranched acrylate resin having 2 or more branch points in a main skeleton thereof and having 9 or more and 16 or less functional groups in a chemical structure thereof; and
0.5 parts by weight or more and 6.0 parts by weight or less of silica particles.
2 . A hard coat film, comprising a resin film and a hard coat layer disposed on a surface of the resin film, wherein
the hard coat layer is a cured product of an ionizing ray polymerizable resin composition, the cured product being produced by curing the ionizing ray polymerizable resin composition by exposure to ionizing rays, the ionizing ray polymerizable resin composition comprising:
65.0 parts by weight or more and 95.0 parts by weight or less of an acrylic component including one or both of a polyfunctional acrylic monomer and a polyfunctional acrylic oligomer having a linear main skeleton or a main skeleton having one branch point;
0.5 parts by weight or more and 12.0 parts by weight or less of a silicone component including one or both of a silicone monomer having an acryloyl group at a terminal thereof and a silicone oligomer having an acryloyl group at a terminal thereof;
2.0 parts by weight or more and 20.0 parts by weight or less of a hyperbranched acrylate resin having 2 or more branch points in a main skeleton thereof and having 9 or more and 16 or less functional groups in a chemical structure thereof; and
0.5 parts by weight or more and 6.0 parts by weight or less of silica particles.
3 . The hard coat film according to claim 2 , wherein the hard coat layer has a thickness of 6.0 mm or more and 12.0 mm or less.
4 . The hard coat film according to claim 2 , wherein an average particle size of the silica particles is 10 nm or more and 50 nm or less.
5 . The hard coat film according to claim 3 , wherein an average particle size of the silica particles is 10 nm or more and 50 nm or less.