Epoxy resin composition, prepreg, and metal-clad laminate and multilayered printed wiring board
The present invention provides an epoxy resin composition exhibiting good workability in drilling, molding, and desmearing as well as good interlayer adhesion strength. This epoxy resin composition comprises an epoxy resin, a curing agent, and an inorganic filler. The epoxy resin is composed of a dicyclopentadiene-based epoxy resin and a novolac-based epoxy resin. The curing agent is a biphenyl-based phenol resin. The inorganic filler is composed of aluminum hydroxide and granular silica having an epoxy-silane treated surface. The epoxy resin composition contains 20 to 50% by weight of the granular silica. The epoxy resin composition contains 2 to 15% by weight, based on total weight of granular silica, of the aluminum hydroxide.
1. An epoxy resin composition comprising an epoxy resin, a curing agent, and an inorganic filler,
said epoxy resin being composed of a dicyclopentadiene-based epoxy resin and a novolac-based epoxy resin,
said curing agent being a biphenyl-based phenol resin,
said inorganic filler being composed of aluminum hydroxide and granular silica having an epoxy-silane treated surface,
wherein the epoxy resin composition contains 20 to 50% by weight, based on the total weight of the epoxy resin composition, of said granular silica, and
wherein the epoxy resin composition contains 2 to 15% by weight, based on total weight of said granular silica, of said aluminum hydroxide.
2. A prepreg comprising a substrate impregnated with said epoxy resin composition as defined in claim 1 , wherein said epoxy resin composition being heated and dried to a semi-cured state.
3. A metal-clad laminate comprising the prepreg of claim 2 , and a metal foil superimposed at least one of opposite surfaces of the prepreg and heat-pressed thereon.
4. A multilayered printed wiring board comprising the metal-clad laminate of claim 3 , wherein said metal-clad laminate is formed with a conductor pattern for use as a core member.
5. The epoxy resin composition of claim 1 , wherein the epoxy resin further contains an inflammable halogenated epoxy resin.
6. The epoxy resin composition of claim 1 , wherein the mass ratio of dicyclopentadiene-based epoxy resin to novolac-based epoxy resin is from 3:1 to 1:3.
7. The epoxy resin composition of claim 1 , wherein the epoxy resin composition contains 15 to 60% by weight, based on total weight of the composition, of said curing agent.
8. The epoxy resin composition of claim 1 , wherein the epoxy resin composition contains 46% by weight, based on the total weight of the composition, of said granular silica, and
wherein the epoxy resin composition contains 14.9% by weight, based on total weight of said granular silica, of said aluminum hydroxide.
9. The epoxy resin composition of claim 1 , wherein the epoxy resin composition contains 49% by weight, based on the total weight of the composition, of said granular silica, and
wherein the epoxy resin composition contains 2.1% by weight, based on total weight of said granular silica, of said aluminum hydroxide.
10. The epoxy resin composition of claim 1 , wherein the epoxy resin composition contains 21% by weight, based on the total weight of the composition, of said granular silica, and
wherein the epoxy resin composition contains 14.9% by weight, based on total weight of said granular silica, of said aluminum hydroxide.
11. The epoxy resin composition of claim 1 , wherein the epoxy resin composition contains 21% by weight, based on the total weight of the composition, of said granular silica, and
wherein the epoxy resin composition contains 2.1% by weight, based on total weight of said granular silica, of said aluminum hydroxide.