Positive electrode mixture for nonaqueous battery and positive electrode structure
A positive electrode mixture for nonaqueous batteries, is formed by adding 0.5 to 10 wt. parts of an organic acid per 100 wt. parts of an electroconductive additive, to a mixture of a composite metal oxide as a positive electrode active substance, a higher order-structured carbon black as the electroconductive additive, a binder of a fluorine-containing copolymer of at least three comonomers including vinylidene fluoride, tetrafluoroethylene and a flexibility-improving fluorine-containing monomer, and an organic solvent. Further, the mixture is applied on at least one side of an electroconductive sheet, and then dried and compressed to form a positive electrode mixture layer. As a result, it is possible to provide a positive electrode structure having a thick and sound positive electrode mixture layer of a high energy density.
1. A positive electrode structure for nonaqueous batteries, comprising: an electroconductive sheet and a 100-149 μm thick dried and compressed positive electrode mixture layer disposed on at least one side of the electroconductive sheet;
wherein the positive electrode mixture layer has been formed by drying and compressing a mixture of a composite metal oxide as a positive electrode active substance, a higher order-structured carbon black as an electroconductive additive, a binder comprising a fluorine-containing copolymer of at least three comonomers including vinylidene fluoride, tetrafluoro-ethylene and a flexibility-improving fluorine-containing monomer selected from hexafluoropropylene and perfluoroalkyl vinyl ether, an organic solvent, and 0.5 to 10 wt. parts of an organic acid per 100 wt. parts of the electroconductive additive,
wherein the higher order-structured carbon black has a specific surface area of at least 500 m 2 /g according to a BET method and a dibutyl phthalate oil absorption of at least 300 ml/100 g, and
the dried and compressed positive electrode mixture layer exhibits a crack-free windability about a round bar of 3 mm in diameter.
2. The positive electrode structure according to claim 1 , wherein the electroconductive additive is contained in 0.1 to 10 wt. parts per 100 wt. parts of the positive electrode active substance.
3. The positive electrode structure according to claim 1 , wherein the fluorine-containing copolymer is contained in 1 to 10 wt. parts per 100 wt. parts of the positive electrode active substance.
4. The positive electrode structure according to claim 1 , wherein the organic acid is at least one member selected from the group consisting of acrylic acid, formic acid, citric acid, acetic acid, oxalic acid, lactic acid, pyruvic acid, malonic acid, propionic acid, maleic acid, citraconic acid, and butyric acid.
5. The positive electrode structure according to claim 4 , wherein the organic acid is selected from oxalic acid and maleic acid.
6. The positive electrode structure according to claim 1 , wherein the composite metal oxide has been neutralized in advance.
7. The positive electrode structure according to claim 1 , in a further wound state.
8. The positive electrode structure according to claim 1 , wherein the binder comprises a fluorine-containing copolymer selected from the group consisting of copolymers of vinylidene fluoride, and tetrafluoro-ethylene with at least one flexibility-improving fluorine-containing monomer selected from hexafluoropropylene and perfluoroalkyl vinyl ether.
9. The positive electrode structure according to claim 1 , wherein the dried and compressed positive electrode mixture layer has a thickness of 123-149 μm.
10. The positive electrode structure according to claim 8 , wherein the dried and compressed positive electrode mixture layer has a thickness of 123-149 μm.