Heat/light-stabilized polyamide compositions
Heat- and light-stabilized polyamide compositions contain a stabilization system that includes copper oxide and KBr, and have an excellent preservation of color and of the mechanical properties thereof after exposure to heat or to light; these compositions are especially useful for producing shaped articles in the automotive field.
1. A color and mechanically stable composition comprising a matrix of at least one polyamide having an apparent viscosity in a molten state ranging from 30 to 1200 Pa.s or 30 to 700 Pa.s., measured according to ISO 11443, and an effective heat- and light-stabilizing amount of at least one oxide of copper and potassium bromide (KBr), wherein the polyamide is a branched polyamide or a star polyamide.
2. A color and mechanically stable composition comprising a matrix of at least one polyamide having an apparent viscosity in a molten state ranging from 30 to 1200 Pa.s or 30 to 700 Pa.s., measured according to ISO 11443, and an effective heat- and light-stabilizing amount of at least one oxide of copper and potassium bromide (KBr), wherein said at least one oxide of copper comprises Cu 2 O, wherein the polyamide is a branched polyamide or a star polyamide.
3. The color/mechanically stable polyamide composition as defined by claim 1 , wherein said at least one oxide of copper comprises CuO.
4. The color/mechanically stable polyamide composition as defined by claim 1 , comprising from 0.001% to 2% by weight of said at least one oxide of copper, relative to the total weight of the at least one polyamide.
5. The color/mechanically stable polyamide composition as defined by claim 1 , further comprising at least one other heat and/or light stabilizer selected from the group consisting of KI, hindered phenolic compounds, stabilizers including at least one hindered amine structural unit, organic or inorganic phosphorus-containing stabilizers, sodium hypophosphite and manganese hypophosphite.
6. The color/mechanically stable polyamide composition as defined by claim 1 , comprising from 0.009% to 1.2% by weight of Cu 2 O and from 0.1% to 1.2% by weight of KBr, relative to the weight of the at least one polyamide.
7. The color/mechanically stable polyamide composition as defined by claim 1 , wherein said polyamide comprises at least one PA-6 polyamide or at least one PA-6,6 polyamide.
8. The color/mechanically stable polyamide composition as defined by claim 7 , said at least one polyamide having an apparent melt viscosity ranging from 30 to 1,200 Pa.s, measured according to the ISO 11443 standard at a shear rate of 1000 s −1 and a temperature of 250° C., for a PA-6 polyamide; or an apparent melt viscosity ranging from 30 to 700 Pa.s, measured according to the ISO 11443 standard at a shear rate of 1000 s −1 and a temperature of 280° C., for a PA-6,6 polyamide.
9. The color/mechanically stable polyamide composition as defined by claim 1 , comprising from 20% to 80% by weight of said at least one polyamide relative to the total weight of the composition.
10. The color/mechanically stable polyamide composition as defined by claim 1 , further comprising fibrous and/or non-fibrous reinforcing filler material.
11. The color/mechanically stable polyamide composition as defined by claim 10 , comprising reinforcing glass fibers.
12. The color/mechanically stable polyamide composition as defined by claim 1 , further comprising impact modifiers.
13. A process for formulating a polyamide composition as defined by claim 1 , in which the at least one polyamide, the at least one copper oxide and the KBr are cold-blended or melt-blended.
14. A shaped article formed from the color/mechanically stable polyamide composition as defined by claim 1 .
15. The color/mechanically stable polyamide composition as defined by claim 1 , comprising a blend of polyamides.
16. The color/mechanically stable polyamide composition as defined by claim 1 , comprising at least one (co)polyamide and/or star polyamide.
17. The shaped article as defined by claim 14 , comprising an automotive shaped article selected from the group consisting of a tank, a part of an air circuit system, an air distributor, an air duct, an turbo outlet duct, a part of a cooling circuit system, an air cooler, a radiator tank and a housing.
18. A color and mechanically stable composition comprising a matrix of at least one polyamide having an apparent viscosity in a molten state ranging from 30 to 1200 Pa.s or 30 to 700 Pa.s., measured according to ISO 11443, and an effective heat- and light-stabilizing amount of at least one oxide of copper and potassium bromide (KBr), wherein the at least one polyamide comprises linkages of isophthalic acid or benzoic acid, wherein said isophthalic acid or benzoic acid is present in an amount from 0.2% wt % to 1 wt % of the composition.
19. The color/mechanically stable polyamide composition as defined by claim 18 , wherein said at least one oxide of copper comprises CuO.
20. The color/mechanically stable polyamide composition as defined by claim 18 , comprising from 0.001% to 2% by weight of said at least one oxide of copper, relative to the total weight of the at least one polyamide.
21. The color/mechanically stable polyamide composition as defined by claim 18 , further comprising at least one other heat and/or light stabilizer selected from the group consisting of KI, hindered phenolic compounds, stabilizers including at least one hindered amine structural unit, organic or inorganic phosphorus-containing stabilizers, sodium hypophosphite and manganese hypophosphite.
22. The color/mechanically stable polyamide composition as defined by claim 18 , comprising from 0.009% to 1.2% by weight of Cu 2 O and from 0.1% to 1.2% by weight of KBr, relative to the weight of the at least one polyamide.
23. The color/mechanically stable polyamide composition as defined by claim 18 , wherein said polyamide comprises at least one PA-6 polyamide or at least one PA-6,6 polyamide.
24. The color/mechanically stable polyamide composition as defined by claim 23 , said at least one polyamide having an apparent melt viscosity ranging from 30 to 1,200 Pa.s, measured according to the ISO 11443 standard at a shear rate of 1000 s −1 and a temperature of 250° C., for a PA-6 polyamide; or an apparent melt viscosity ranging from 30 to 700 Pa.s, measured according to the ISO 11443 standard at a shear rate of 1000 s −1 and a temperature of 280° C., for a PA-6,6 polyamide.
25. The color/mechanically stable polyamide composition as defined by claim 18 , comprising from 20% to 80% by weight of said at least one polyamide relative to the total weight of the composition.
26. The color/mechanically stable polyamide composition as defined by claim 18 , further comprising fibrous and/or non-fibrous reinforcing filler material.
27. The color/mechanically stable polyamide composition as defined by claim 26 , comprising reinforcing glass fibers.
28. The color/mechanically stable polyamide composition as defined by claim 18 , further comprising impact modifiers.
29. A process for formulating a polyamide composition as defined by claim 18 , in which the at least one polyamide, the at least one copper oxide and the KBr are cold-blended or melt-blended.
30. A shaped article formed from the color/mechanically stable polyamide composition as defined by claim 18 .
31. The color/mechanically stable polyamide composition as defined by claim 18 , comprising a blend of polyamides.
32. The color/mechanically stable polyamide composition as defined by claim 18 , comprising at least one (co)polyamide and/or star polyamide.
33. The shaped article as defined by claim 30 , comprising an automotive shaped article selected from the group consisting of a tank, a part of an air circuit system, an air distributor, an air duct, an turbo outlet duct, a part of a cooling circuit system, an air cooler, a radiator tank and a housing.
34. A color and mechanically stable composition comprising a matrix of at least one polyamide having an apparent viscosity in a molten state ranging from 30 to 1200 Pa.s or 30 to 700 Pa.s., measured according to ISO 11443, and an effective heat- and light-stabilizing amount of at least one oxide of copper and potassium bromide (KBr), wherein said at least one oxide of copper comprises Cu 2 O, wherein the at least one polyamide comprises linkages of isophthalic acid or benzoic acid, wherein said isophthalic acid or benzoic acid is present in an amount from 0.2% wt % to 1 wt % of the composition.