Modified zeolite Y membranes for high-performance CO
View Patent ↗Supported zeolite Y membranes exhibiting exceptionally high CO2 selectivities when used in CO 2 /N 2 gas separations are produced by a seeding/secondary (hypothermal) growth approach in which a structure directing agent such as tetramethylammonium hydroxide is included in the aqueous crystal-growing composition used for membrane formation.
1. A process for producing a supported zeolite Y membrane for use in a gas separation procedure in which zeolite Y seed crystals previously deposited onto a porous support are grown into a coherent zeolite Y membrane by contact with a zeolite-growing aqueous composition and the coherent zeolite Y membrane so formed is then dried,
wherein the zeolite-growing aqueous composition contains a structure directing agent capable of promoting the formation of zeolite Y, and further
wherein drying of the coherent zeolite Y membrane is done under conditions which cause at least about 70% of the structure directing agent that is present in the membrane when formed to remain in the membrane after drying is completed.
2. The process of claim 1 , wherein the structure directing agent is a tetramethylammonium compound.
3. The process of claim 2 , wherein tetramethylammonium compound contains an anion selected from the group consisting of OH − , Br − , Cl − and F − .
4. The process of claim 3 , wherein at least about 80% of the structure directing agent that is present in the membrane when formed remains in the membrane after drying is completed.
5. The process of claim 4 , wherein at least about 90% of the structure directing agent that is present in the membrane when formed remains in the membrane after drying is completed.
6. The process of claim 5 , wherein substantially all of the structure directing agent that is present in the membrane when formed remains in the membrane after drying is completed.
7. The process of claim 1 , wherein drying of the coherent zeolite Y membrane is done under conditions which cause at least about 80% of the structure directing agent that is present in the membrane when formed to remain in the membrane after drying is completed.
8. The process of claim 1 , wherein drying of the coherent zeolite Y membrane is done under conditions which cause substantially all of the structure directing agent that is present in the membrane when formed to remain in the membrane after drying is completed.
9. A dried supported zeolite Y membrane for use in a gas separation procedure, the supported membrane comprising a porous support and a coherent zeolite Y membrane on the support, the membrane being produced by a seeding/secondary crystal growing process in which zeolite Y seed crystals previously deposited onto a porous support are grown into a coherent zeolite Y membrane by contact with a zeolite-growing aqueous composition and the coherent zeolite Y membrane so formed is then dried,
wherein the zeolite-growing aqueous composition contains a structure directing agent capable of promoting the formation of zeolite Y and further wherein drying of the coherent zeolite Y membrane is done under conditions which cause at least about 70% of the structure directing agent that is present in the membrane when formed to remain in the membrane after drying is completed.
10. The dried supported zeolite Y membrane of claim 9 , wherein the structure directing agent is a tetramethylammonium compound.
11. The dried supported zeolite Y membrane of claim 10 , wherein tetramethylammonium compound contains an anion selected from the group consisting of OH − , Br − , Cl − and F − .
12. The dried supported zeolite Y membrane of claim 9 , wherein at least about 80% of the structure directing agent that is present in the membrane when formed remains in the membrane after drying is completed.
13. The dried supported zeolite Y membrane of claim 12 , wherein at least about 90% of the structure directing agent that is present in the membrane when formed remains in the membrane after drying is completed.
14. The dried supported zeolite Y membrane of claim 13 , wherein substantially all of the structure directing agent that is present in the membrane when formed remains in the membrane after drying is completed.
15. A process for separating a gas mixture into its component parts comprising contacting the gas mixture with the dried supported zeolite Y membrane of claim 9 .
16. The process of claim 15 , wherein CO 2 is separated from a gas mixture containing at least CO 2 and N 2 .
17. A process for separating a gas mixture into its component parts comprising contacting the gas mixture with the supported zeolite Y membrane of claim 12 .
18. The process of claim 17 , wherein CO 2 is separated from a gas mixture containing at least CO 2 and N 2 .
19. A process for separating a gas mixture into its component parts comprising contacting the gas mixture with the supported zeolite Y membrane of claim 14 .
20. The process of claim 19 , wherein CO 2 is separated from a gas mixture containing at least CO 2 and N 2 .