Extended wear ophthalmic lens
An ophthalmic lens suited for extended-wear periods of at least one day on the eye without a clinically significant amount of corneal swelling and without substantial wearer discomfort. In one embodiment, an ophthalmic lens is a copolymerization product of at least one oxyperm, at least one ionoperm, and a crosslinker. In one embodiment, a lens has a tensile modulus of less than about 3.0 MPa, yet in another embodiment, the tensile modulus is between about 0.5 to about 1.5 MPa.
1. A contact lens, comprising:
a core polymeric material formed from polymerization of a prepolymerization mixture including: (i) one or more oxyperm macromers or monomers selected from the group consisting of siloxane-containing macromers and monomers, fluorine-containing macromers and monomers, carbon-carbon triple bond-containing macromers and monomers, and combinations thereof; (ii) an ionoperm polymerizable material including at least one hydrophilic monomer; (iii) less than 5% by weight of a cross-linking agent other than component (i); and (iv) a solvent,
wherein the contact lens has a diameter of 13 to 15 mm and a center thickness of 40 to 150 microns, and wherein the one or more oxyperm macromers or monomers and the ionoperm polymerizable material are present in the prepolymerization mixture in an amount sufficient to provide the contact lens an oxygen transmissibility of at least 70 barrers/mm, an ion permeability characterized by an Ionoflux Ion Permeability Coefficient of greater than 6.4×10 −6 mm 2 /min, and a tensile modulus of 0.5 to 1.5 MPa, and to provide the contact lens with an ability to be worn for a continuous period of at least 24 hours including a normal sleep period and during which the lens exhibits on-eye movement with blinking and produces less than 8% corneal swelling after the continuous period of wear.
2. The contact lens of claim 1 , wherein said one or more oxyperm macromers or monomers are siloxane-containing macromers or monomers.
3. The contact lens of claim 2 , wherein the siloxane-containing macromers or monomers contain one or more hydrophilic groups.
4. The contact lens of claim 3 , wherein the hydrophilic groups are selected from the group consisting of: polyoxyethylene, urethane, urea, amide, amine, hydroxyl and combinations thereof.
5. The contact lens of claim 4 , wherein said at least one hydrophilic monomer is selected from the group consisting of hydroxyl-substituted lower alkyl acrylate and methacrylate, acrylamide, methacrylamide, (lower alkyl)-acrylamide and -methacrylamide, ethoxylated acrylate and methacrylate, hydroxyl-substituted (lower alkyl)-acrylamide and -methacrylamide, hydroxyl-substituted lower alkyl vinyl ether, sodium vinylsulfonate, sodium styrenesulfonate, 2-acrylamido-2-methylpropanesulfonic acid, N-vinylpyrrole, N-vinyl-2-pyrrolidone, 2-vinyloxazoline, 2-vinyl-4,4′-dialkyloxazolin-5-one, 2- and 4-vinylpyridine, vinylically unsaturated carboxylic acids having a total of 3 to 5 carbon atoms, amino(lower alkyl)-acrylate and methacrylate, mono(lower alkylamino)(lower alkyl)-acrylate and methacrylate, di(lower alkylamino)(lower alkyl)-acrylate and methacrylate, allyl alcohol, and combinations thereof.
6. The contact lens of claim 3 , wherein said at least one hydrophilic monomer is hydroxyethyl methacrylate, hydroxyethyl acrylate, hydroxypropyl acrylate, trimethylammonium 2-hydroxy propylmethacrylate hydrochloride, dimethylaminoethyl methacrylate, dimethylaminoethylmethacrylamide, acrylamide, methacrylamide, N,N-dimethylacrylamide, allyl alcohol, vinylpyridine, glycerol methacrylate, N-(1,1-dimethyl-3-oxobutyl)acrylamide, N-vinyl-2-pyrrolidone, acrylic acid, or methacrylic acid.
7. The contact lens of claim 6 , wherein said at least one hydrophilic monomer is hydroxyethyl methacrylate, N,N-dimethylacrylamide, or N-vinyl-2-pyrrolidone.
8. The contact lens of claim 6 , wherein the cross-linking agent is selected from the group consisting of allyl(meth)acrylate, C 1 -C 6 alkylene glycol di(meth)acrylate, poly C 1 -C 6 alkylene glycol di(meth)acrylate, C 1 -C 6 alkylene di(meth)acrylate, divinyl ether, divinyl sulfone, divinylbenzene, trivinylbenzene, trimethylolpropane tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, bisphenol A di(meth)acrylate, methylenebis(meth)acrylamide, triallyl phthalate, diallyl phthalate and combinations thereof.
9. The contact lens of claim 8 , wherein the cross-linking agent is present in the prepolymerization mixture in an amount of less than 2% by weight.
10. The contact lens of claim 6 , wherein the prepolymerization mixture comprises at least one hydrophobic monomer selected from the group consisting of methyl acrylate, ethyl acrylate, propyl acrylate, isopropyl acrylate, isobutyl acrylate, isooctyl acrylate, isodecyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl acrylate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl valerate, styrene, chloroprene, vinyl chloride, vinylidene chloride, acrylonitrile, 1-butene, butadiene, methacrylonitrile, vinyl toluene, vinyl ethyl ether, perfluorohexylethylthiocarbonylaminoethyl methacrylate, isobornyl methacrylate, trifluoroethyl methacrylate, hexafluoroisopropyl methacrylate, hexafluorobutyl(meth)acrylate, tris-trimethylsilyloxy-silyl-propyl methacrylate (TRIS), 3-methacryloxypropylpentamethyldisiloxane, bis(methacryloxypropyl) tetramethyldisiloxane and combinations thereof.
11. The contact lens of claim 10 , wherein the hydrophobic monomer is tris-trimethylsilyloxy-silyl-propyl methacrylate (TRIS).
12. The contact lens of claim 6 , wherein the contact lens includes a surface that is more hydrophilic than the core polymeric material of the contact lens.
13. The contact lens of claim 12 , wherein one or more surface properties of the contact lens are altered by a surface treatment process.
14. The contact lens of claim 13 , wherein the surface treatment process is performed prior to and/or posterior to complete polymerization of the prepolymerization mixture.
15. The contact lens of claim 12 , wherein the contact lens has an ability to be worn for a continuous period of wear of at least 24 hours including a normal sleep period during which the lens exhibits on-eye movement with blinking and produces less than 6% corneal swelling after the continuous period of wear.
16. The contact lens of claim 15 , wherein the contact lens has an ability to be worn for a continuous period of wear of at least 24 hours including a normal sleep period during which the lens exhibits on-eye movement with blinking and produces less than 4% corneal swelling after the continuous period of wear.