Process for preparing a foaming slag former, product and use thereof
Process for preparing a foaming slag former for electric furnaces comprising the steps of aggregating solid slag particles into a coarser granular material and carbonating the solid slag particles to form the foaming slag former. The solid slag particles are preferably aggregated before carbonization, so that the carbonates form a solid matrix binding the particles together.
1. Process for preparing a foaming slag former ( 40 ) for electric arc furnaces ( 1 ), with at least 20 wt. % of solid slag particles, characterised in that it comprises the steps of: aggregating said solid slag particles to form a granular material formed by coarser grains, and carbonating said solid slag particles, after being aggregated in said aggregating step, to produce said slag former ( 40 ).
2. Process according to claim 1 , wherein during said carbonating step at least 2 wt. % of carbonates are produced.
3. Process according to claim 1 , wherein said carbonating is carried out with a gas comprising at least 5 vol. % of carbon dioxide.
4. Process according to claim 3 , wherein said gas comprises less than 30 vol. % of carbon dioxide.
5. Process according to claim 3 , wherein said carbonating step is performed at a temperature of between 10 and 100° C.
6. Process according to claim 3 , wherein said carbonating step is performed at a pressure lower than 10 bar.
7. Process according to claim 3 , wherein after said carbonating said gas is used to reduce alkalinity of an effluent water having a pH higher than 11.
8. Process according to claim 1 , wherein said slag particles have sizes not larger than x, said x being not larger than 4 mm.
9. Process according to claim 1 , wherein said coarser grains have sizes not smaller than y, said y being not smaller than 1 mm.
10. Process according to claim 1 , wherein a binder is added during and/or before said aggregating step to help bind the slag particles together into the coarser grains.
11. Process according to claim 1 , wherein said granular material contains sand ( 32 ).
12. Process according to claim 1 , wherein said coarser grains contain carbonaceous particles.
13. Process according to claim 1 , wherein said coarser grains contain bauxite particles.
14. Process according to claim 1 , wherein said coarser grains contain stone crushing sands and/or dust.
15. Process according to claim 1 , wherein said coarser grains contain glass particles.
16. Process according to claim 1 , wherein said slag particles contain a significant amount of γ-dicalcium silicate.
17. Process according to claim 1 , wherein said slag particles are from stainless steel slag.
18. Process according to claim 1 , wherein said aggregating step comprises aggregating said solid slag particles into a block and then, after said carbonating step, breaking up said block to produce said granular material.
19. Process according to claim 1 , wherein said slag particles contain at least 3 wt. % of γ-dicalcium silicate.
20. Foaming slag former ( 40 ) for electric arc furnaces ( 1 ) prepared according to claim 1 , wherein the foaming slag former ( 40 ) comprises carbonated solid slag particles aggregated to form a granular material formed by coarser grains.
21. Method of forming a slag on a melt in an electric arc furnace ( 1 ), said method comprising adding a foaming slag former ( 40 ) prepared according to claim 1 to said electric arc furnace ( 1 ).
22. Method according to claim 21 , wherein said foaming slag former ( 40 ) is introduced into said electric arc furnace ( 1 ) through at least one chute ( 45 ) and/or at least one trough lance ( 46 ).
23. Method according to claim 21 , wherein said foaming slag former ( 40 ) is introduced into said electric arc furnace (I) concurrently with a carbonaceous material.