Method of forming a polymer component
This invention relates to a method of forming a polymer component and comprises blending polymer particles with antioxidant to form a mixture in which the antioxidant coats the polymer particles, irradiating the mixture to cross-link the polymer particles therein and forming the irradiated mixture into a consolidated component. The invention also relates to a method of forming an articular surface for a prosthesis and a prosthesis having a polymer articular bearing surface wherein at least one pre-determined portion of the bearing surface is provided with cross-linked polymer bonds.
1. A prosthesis comprising:
a shell; and
disposed on the shell, a polymer liner having a concave articular bearing surface opposite the shell, the polymer liner comprising (i) a first cross-linked polymer region and (ii) a second substantially non-cross-linked polymer region molded to the first cross-linked polymer region,
wherein (i) exposed portions of the first cross-linked polymer region and the second substantially non-cross-linked polymer region collectively define the concave articular bearing surface, (ii) the exposed portion of the first cross-linked polymer defines a pre-determined wear zone of the concave articular bearing surface, (iii) the pre-determined wear zone does not extend along the entire concave articular bearing surface, (iv) the concave articular bearing surface of the polymer liner terminates at non-concave edges, wherein an exposed surface of a non-concave edge is defined only by an exposed surface of the second substantially non-cross-linked polymer, and (v) the second substantially non-cross-linked polymer region includes a rounded edge that extends over the edge of the shell.
2. The prosthesis according to claim 1 wherein a thickness of the polymer liner in the region of the pre-determined wear zone is larger than a thickness of the polymer liner outside of the pre-determined wear zone.
3. The prosthesis according to claim 1 wherein multiple protrusions are provided at an interface between the first cross-linked polymer region and the second substantially non-cross-linked polymer region.
4. A prosthesis comprising:
a shell; and
disposed on the shell, a polymer liner having a concave articular bearing surface opposite the shell, the polymer liner comprising (i) a first cross-linked polymer region and (ii) a second substantially non-cross-linked polymer region molded to the first cross-linked polymer region,
wherein (i) exposed portions of the first cross-linked polymer region and the second substantially non-cross-linked polymer region collectively define the concave articular bearing surface, (ii) the exposed portion of the first cross-linked polymer defines a pre-determined wear zone of the concave articular bearing surface, (iii) the pre-determined wear zone does not extend along the entire concave articular bearing surface, (iv) multiple protrusions are provided at an interface between the first cross-linked polymer region and the second substantially non-cross-linked polymer region, and (v) the protrusions are in the form of ridges or fingers.
5. A. prosthesis comprising:
a shell; and
disposed on the shell, a polymer liner having a concave articular bearing surface opposite the shell, the polymer liner comprising (i) a first cross-linked polymer region and (ii) a second substantially non-cross-linked polymer region molded to the first cross-linked polymer region.
wherein (i) exposed portions of the first cross-linked polymer region and the second substantially non-cross-linked polymer region collectively define the concave articular bearing surface, (ii) the exposed portion of the first cross-linked polymer defines a pre-determined wear zone of the concave articular bearing surface, (iii) the pre-determined wear zone does not extend along the entire concave articular bearing surface, (iv) multiple protrusions are provided at an interface between the first cross-linked polymer region and the second substantially non-cross-linked polymer region, and (v) the protrusions are provided by introducing roughness at the interface between the first cross-linked polymer region and the second substantially non-cross-linked polymer region.
6. The prosthesis according to claim 1 wherein the prosthesis is configured as an acetabular cup.
7. The prosthesis according to claim 6 wherein the shell is a metal shell.